Influence of heat-treatment on oxidation-resistance of phosphate-coating for C/C composite

Phosphate-coating was prepared for C/C composite using liquid-impregnation and different heat-treatment. The results show that the mass-loss rate of sample A with 1-2 degrees C/min slow-cooling rate technology is 47% after oxidation at 700 degrees C for 20 h, while that of sample B with air-fast-cooling one is only 0.98%. SEM images reveal that the coating of sample A is full of micro-holes, micro-cracks and many piece-like crystal particles, while that of sample B is integrated and compacted in glassy state with a few of micro-cracks. The coating of sample A is almost exhausted only in 8 h oxidized-test at 700 degrees C, while that of sample B remains integrated after 8 h test at 700 degrees C and becomes loose due to much small pores generated after 20 h test at 700 degrees C.