Fracture characteristics of γ-TiAl alloy with high Nb content under cyclic loading

被引：25

作者：

Cui, W. F. ^{[1
]}

Liu, C. M. ^{[1
]}

机构：

[1] Northeastern Univ, Coll Mat & Met, Shenyang 110004, Peoples R China

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2009年 / 477卷 / 1-2期

关键词：

Low cycle fatigue; Temperature; Fracture; Environmental effects; gamma-TiAl alloy; FATIGUE-CRACK GROWTH; TITANIUM ALUMINIDE ALLOYS; TEMPERATURE; BEHAVIOR; MICROSTRUCTURE; PROPAGATION; ENVIRONMENT;

D O I：

10.1016/j.jallcom.2008.10.118

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

This work investigates the isothermal low cycle fatigue (LCF) behavior of a third generation gamma-TiAl-based alloy with duplex microstructure under the various test conditions, including temperature (550-750 degrees C), total strain amplitude (0.3-0.6%) and environment (air and vacuum) in order to clarify the relationships among the fatigue life, plastic deformation character and fracture process. The plastic strain accumulation during cyclic loading has a great contribution to LCF damage. Under the small total strain amplitude (<= 0.4%), the increase of test temperature enforces microstructure resistance to LCF fracture. However, under the large total strain amplitude (>= 0.5%) the increase of test temperature accelerates the microstructural degradation process that behaves the dissolution Of alpha(2) lamellae and coarsening of gamma grains, and results in great LCF damage. Moreover, the environment brittlement during high temperature exposure to air influences the initiation rate of fatigue cracks and shortens LCF life. The paper also discussed the LCF fracture mechanisms of gamma-TiAl alloy at various temperatures. (C) 2008 Elsevier B.V. All rights reserved.

引用

页码：596 / 601

页数：6

共 19 条

[1] Novel design concepts for gamma-base titanium aluminide alloys [J].

Appel, F ;

Oehring, M ;

Wagner, R .

INTERMETALLICS, 2000, 8 (9-11) :1283-1312

[2] Microstructure-low cycle fatigue behaviour relationships in a PM γ-TiAl alloy [J].

Berteaux, O. ;

Jouiad, M. ;

Thomas, M. ;

Henaff, G. .

INTERMETALLICS, 2006, 14 (10-11) :1130-1135

[3] Designed fully lamellar microstructures in a γ-TiAl based alloy:: adjustment and micro, structural changes upon long-term isothermal exposure at 700 and 800°C [J].

Beschliesser, M ;

Chatterjee, A ;

Lorich, A ;

Knabl, W ;

Kestler, H ;

Dehm, G ;

Clemens, H .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 329 :124-129

[4] High-temperature fatigue behavior of a near-γ titanium aluminide alloy under isothermal and thermo-mechanical conditions [J].

Christ, HJ ;

Fischer, FOR ;

Maier, HJ .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 319 :625-630

[5] Thermomechanical fatigue behaviours of a third generation γ-TiAl based alloy [J].

Cui, W. F. ;

Liu, C. M. ;

Bauer, V. ;

Christ, Ha. .

INTERMETALLICS, 2007, 15 (5-6) :675-678

[6] Low-cycle fatigue and deformation substructures in an engineering TiAl alloy [J].

Gloanec, A. L. ;

Jouiad, M. ;

Bertheau, D. ;

Grange, M. ;

Henaff, G. .

INTERMETALLICS, 2007, 15 (04) :520-531

[7] Fatigue crack growth behavior of equiaxed, duplex and lamellar microstructure gamma-base titanium aluminides [J].

Gnanamoorthy, R ;

Mutoh, Y ;

Mizuhara, Y .

INTERMETALLICS, 1996, 4 (07) :525-532

[8]

LESTERIN S, 1997, P 9 INT C FAT SIDN, P36

[9] ROOM-TEMPERATURE ENVIRONMENTAL EMBRITTLEMENT IN A TIAL ALLOY [J].

LIU, CT ;

KIM, YW .

SCRIPTA METALLURGICA ET MATERIALIA, 1992, 27 (05) :599-603

[10] An investigation of the effects of temperature on fatigue crack growth in a cast lamellar Ti-45Al-2Mn-2Nb+0.8 vol.% TiB2 alloy [J].

Lou, J ;

Mercer, C ;

Soboyejo, WO .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 319 :618-624

← 1 2 →