Preparation and microstructure of in situ particle reinforced titanium matrix alloy

被引:22
作者
Zhang, EL [1 ]
Zeng, SY
Wang, B
机构
[1] Brunel Univ, Dept Mech Engn, Uxbridge UB8 3PH, Middx, England
[2] Harbin Inst Technol, Natl Key Lab Precious Hot Proc Met, Harbin 150001, Peoples R China
关键词
titanium matrix composites; hardness; microstructures; casting;
D O I
10.1016/S0924-0136(02)00329-1
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Ti-6Al/TiC, Ti-6Al/TiB and Ti-6Al/TiC + TiB have been manufactured by an in situ method. X-ray diffraction (XRD), optical microscopy and scanning electron microscopy (SEM) have been used to identify the phases and observe the morphologies and distribution characteristics of TiC and TiB with the change of the alloy composition. In Ti-6Al-(0.4-2.0)C alloys, TiC appears mainly to be rod-like shape in low C content alloys and coarse dendritic shape in higher C content alloys, respectively. The rod-like shape TiC has a tendency to segregate at the grain boundary. It was also shown that the Al content has great influence on the phase constitute and the reinforcement morphology. In Ti-6Al-(0.3-1.2)B alloys, TiB was formed as reinforcement and the in situ TiB is mainly fibrous. But in higher B content alloys, some hollow TiB fibres were also formed. The distribution and the size of TiB are very sensitive to the cooling rate. In TiC + TiB reinforced composites, TiC and TiB still remain dendritic and fibrous, respectively. However, the coexistence of TiC and TiB slightly reduces the scale of the reinforcements. The microhardness was found to have little dependence on the morphology of reinforcements. (C) 2002 Elsevier Science B.V All rights reserved.
引用
收藏
页码:103 / 109
页数:7
相关论文
共 12 条
[1]   The kinetics and mechanism of interfacial reaction in sigma fibre-reinforced Ti MMCs [J].
Fan, Z ;
Guo, ZX ;
Cantor, B .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1997, 28 (02) :131-140
[2]   MICROSTRUCTURE EVOLUTION IN TIAL ALLOYS WITH B-ADDITIONS - CONVENTIONAL SOLIDIFICATION [J].
HYMAN, ME ;
MCCULLOUGH, C ;
VALENCIA, JJ ;
LEVI, CG ;
MEHRABIAN, R .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (09) :1847-1859
[3]  
KUMAR KS, 1992, MATER SCI TECH SER, V8, P317, DOI 10.1179/026708392790170829
[4]  
KUMAR KS, 1995, ADV MAT P, V4, P35
[5]  
LEWIS D, 1995, ADV MATER PROCESS, V7, P29
[6]   THE EFFECT OF MATRIX REINFORCEMENT REACTION ON FRACTURE IN TI-6AL-4V-BASE COMPOSITES [J].
LORETTO, MH ;
KONITZER, DG .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (06) :1579-1587
[7]  
MURRAY JL, 1986, BINARY ALLOY PHASE
[8]  
Pietzka MA., 1994, J. Phase Equilib, V15, P392, DOI [10.1007/BF02647559, DOI 10.1007/BF02647559]
[9]  
Ranganath S, 1997, J MATER SCI, V32, P1
[10]   Evolution of microstructure and phases in in situ processed Ti-TiB composites containing high volume fractions of TiB whiskers [J].
Sahay, SS ;
Ravichandran, KS ;
Atri, R ;
Chen, B ;
Rubin, J .
JOURNAL OF MATERIALS RESEARCH, 1999, 14 (11) :4214-4223