g-C3N4/TiO2 hybrid film on the metal surface, a cheap and efficient sunlight active photoelectrochemical anticorrosion coating

A solar light active photoelectrochemical anticorrosion paint was prepared by dispersing g-C3N4 nanomaterial in 0.05M TiO(Acac)(2) solution. The paint can form uniform film on the metal surface after paralysis, which can provide effective cathodic protection for 304 SS under visible light irradiation. UV-Vis, Powder XRD, IR and EDS characterization identified that the film was composed by g-C3N4 and amorphous TiO2; After coating the g-C3N4/TiO2 film, which has a thickness around 12 um as shown by SEM, a photo-potential up to 0.20V was observed for the metal specimen under visible light illumination (30mW/cm(2)) in 3% NaCl solution. The photo-potential can be accumulated with the irradiation time and held for many hours after removing the light illumination. Effective full-day cathodic protection for 304 SS can be provided by this g-C3N4/TiO2 coating.