Comparison of nitrogen alloyed austenitic steels and high strength armor steels impacted at high velocity

被引：25

作者：

Lach, E ^{[1
]}

Koerber, G ^{[1
]}

Scharf, M ^{[1
]}

Bohmann, A ^{[1
]}

机构：

[1] German French Res Inst St Louis, D-79574 Weil, Germany

来源：

INTERNATIONAL JOURNAL OF IMPACT ENGINEERING | 1999年 / 23卷 / 01期

关键词：

D O I：

10.1016/S0734-743X(99)00100-1

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The ballistic performance of a work hardened nitrogen alloyed austenitic steel (P900) was studied by a light gas gun at a projectile velocity of 2500 m/s. To compare ballistic efficiency and residual microstructure to classical martensitic armor steels, tests with a high hardness armor steel were performed. The hardness of the work hardened P900 and the armor steel were 380 HV30 and 500 HV30, respectively. Both steels proved to offer an identical ballistic performance. Measurements of hardness around the crater have shown a strong increase of hardness for P900 whereas the hardness of the armor steel did not change. Compression tests on a split-Hopkinson-pressure-bar show that nitrogen alloyed austenitic steel strain harden very strongly and possess very high strain rate sensitivity. Strain hardening and strain rate sensitivity of high hardness armor steels are very small. Grain sizes in the heat-affected zone near the crater of nitrogen alloyed steels give information about temperature and heating time. (C) 1999 Elsevier Science Ltd. All rights reserved.

引用

页码：509 / 517

页数：9

共 10 条

[1] FEICHTINGER HK, 1993, P 3 INT C KIEW 1993
[2] LACH E, 1997, J PHYSIQUE, V4, P547
[3] LACH E, 1997, R12997 ISL
[4] LICHTENBERGER A, 1998, P DYM TECHN M DIJ OC
[5] LICHTENBERGER A, 1997, J PHYSIQUE, V4, P391
[6] PAULUS N, 1994, THESIS ETH ZURICH ZU
[7] Speidel MO, 1991, ERGEBNISSE WERKSTOFF, V4
[8] Stein G, 1988, SPECIAL MELTING PROC
[9] UGGOWITZER PJ, 1992, THESIS ETH ZURICH
[10] 1970, MATERIALPRUFNORMEN M

← 1 →