Mitigation of Intergranular Cracking in Al-Mg Alloys via Zn-Based Electrode Potential Control in Sodium Chloride Solution

被引:12
作者
McMahon, M. E. [1 ]
Scully, J. R. [1 ]
Burns, J. T. [1 ]
机构
[1] Univ Virginia, Dept Mat Sci & Engn, Ctr Electrochem Sci & Engn, Charlottesville, VA 22904 USA
关键词
aluminum alloy; cathodic protection; hydrogen embrittlement; inorganic coatings; intergranular stress corrosion cracking; polarization resistance; zinc; STRESS-CORROSION CRACKING; ENVIRONMENTAL DEGRADATION; ASSISTED CRACKING; RICH PRIMER; ALUMINUM; SENSITIZATION; PROPAGATION; PERFORMANCE; ORIENTATION; COATINGS;
D O I
10.5006/3185
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Mitigation of the initiation and propagation of intergranular stress corrosion cracking (IG-SCC) in a single edge notch tensile specimen is achieved through use of various Zn-based anodes on highly sensitized Al-Mg alloy AA5456-H116. Slow-rising displacement tests in an NaCl solution demonstrate the efficacy of cathodic protection through galvanic coupling with pure Zn or an inorganic Zn-rich primer (IOZRP), as well as through spray-coating the fracture specimen with the IOZRP (with various widths of exposed substrate about the Mode I crack path). These tests were conducted in either 0.60 M or 5.45 M NaCl. In all cases, the IG-SCC mitigation performance correlates with the measured coupled potentials, which was corroborated with fixed potential results (via potentiostat). Furthermore, galvanic coupling was able to halt actively propagating IG-SCC (K of 10 MPa root m in 0.60 M NaCl); specifically, the crack growth rate was decreased by three orders of magnitude following the application of cathodic protection. This high level of mitigation is achieved via a potentiostat, coupling with a pure Zn anode (with an exposed area as low as 0.03 cm(2) [1 Zn: 110 AA5456 surface area ratio]), and by coupling with the IOZRP (with an exposed area as low as 0.67 cm(2) [67 primer: 350 AA5456 surface area ratio]). Results are interpreted within the context of a coupled anodic dissolution-hydrogen embrittlement model developed previously.
引用
收藏
页码:911 / 928
页数:18
相关论文
共 39 条
[1]   Effective Hydrogen Diffusion in Aluminum Alloy 5083-H131 as a Function of Orientation and Degree of Sensitization [J].
Ai, Jia-He ;
Lim, Mary Lyn C. ;
Scully, John R. .
CORROSION, 2013, 69 (12) :1225-1239
[2]  
[Anonymous], 2004, G6704 ASTM INT
[3]   Crack Chemistry Control of Intergranular Stress Corrosion Cracking in Sensitized Al-Mg [J].
Crane, Cortney B. ;
Kelly, Robert G. ;
Gangloff, Richard P. .
CORROSION, 2016, 72 (02) :242-263
[4]   Stress Corrosion Cracking of Al-Mg Alloy 5083 Sensitized at Low Temperature [J].
Crane, Cortney B. ;
Gangloff, Richard P. .
CORROSION, 2016, 72 (02) :221-241
[5]   Deterioration of cathodic protection action of zinc-rich paint coatings in atmospheric exposure [J].
Feliu, S ;
Morcillo, M ;
Feliu, S .
CORROSION, 2001, 57 (07) :591-597
[6]  
Gangloff R.P., 1992, SMALL CRACK TEST MET, P116
[7]   Measurement and Modeling of Hydrogen Environment-Assisted Cracking in Monel K-500 [J].
Gangloff, Richard P. ;
Ha, Hung M. ;
Burns, James T. ;
Scully, John R. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (09) :3814-3834
[8]   Influence of Mg Content on the Sensitization and Corrosion of Al-xMg(-Mn) Alloys [J].
Gupta, R. K. ;
Zhang, R. ;
Davies, C. H. J. ;
Birbilis, N. .
CORROSION, 2013, 69 (11) :1081-1087
[9]   Environmental Degradation of Marine Aluminum Alloys-Past, Present, and Future [J].
Holroyd, N. J. Henry ;
Scamans, Geoffrey M. .
CORROSION, 2016, 72 (02) :136-143
[10]   THE ROLE OF MAGNESIUM DURING ENVIRONMENT-SENSITIVE FRACTURE OF ALUMINUM-ALLOYS [J].
HOLROYD, NJH ;
SCAMANS, GM .
SCRIPTA METALLURGICA, 1985, 19 (07) :915-916