Mechanical and thermal properties of hot pressed ZrB2 system with TiB2

被引：65

作者：

Chakraborty, S. ^{[1
]}

Debnath, D. ^{[1
]}

Mallick, A. R. ^{[1
]}

Das, P. K. ^{[1
]}

机构：

[1] CSIR CGCRI, NOCCD, Kolkata 700032, WB, India

来源：

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2014年 / 46卷

关键词：

Zirconium diboride; UHTC; Titanium diboride; Hot pressing; Wear resistance; ZRB2-BASED COMPOSITES; PHYSICAL-PROPERTIES; MICROSTRUCTURE; ZIRCONIUM; CERAMICS; BEHAVIOR; RESISTANCE;

D O I：

10.1016/j.ijrmhm.2014.05.004

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

ZrB2-TiB2-based ceramics with varying amount of TiB2 (up to 30 wt%) were hot pressed at 2200 degrees C in Ar atmosphere, and the effect of the TiB2 addition on mechanical properties like hardness, fracture toughness, scratch resistance, wear resistance and thermal conductivity of the system was compared to monolithic ZrB2 ceramic. It was found from X-ray diffraction that TiB2 completely entered into the structure and formed solid solution with ZrB2. Addition of TiB2 in ZrB2 system improves the mechanical and wear resistance properties. ZrB2-TiB2 (30 wt%) ceramic, for example, showed highest hardness of 22.34 GPa, fracture toughness 3.01 MPa(m)(1/2) and lowest coefficient of friction (0.398 at 10 N load). The addition of TiB2 in ZrB2 system showed lower thermal conductivity than monolithic ZrB2 by increasing grain boundary thermal resistance. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：35 / 42

页数：8

共 36 条