Effect of sand percentage on early-age cracking behaviors of concrete

被引：0
|
作者：
Tang, Fangyu [1 ]
Zhang, Hengchun [1 ]
Ji, Xixian [1 ]
Wu, Xiaoqiang [1 ]
机构：
[1] China State Construct Ready Mixed Concrete Fujian, Fuzhou 350000, Peoples R China
来源：
PROCEEDINGS OF THE 2016 4TH INTERNATIONAL CONFERENCE ON SENSORS, MECHATRONICS AND AUTOMATION (ICSMA 2016) | 2016年 / 136卷
关键词：
concrete; cracking; sand percentage;
D O I：
暂无
中图分类号：
TP18 [人工智能理论];
学科分类号：
081104 ; 0812 ; 0835 ; 1405 ;
摘要：
It was analyzed by using flat-type specimens that studied the influence of sand percentage on early-age cracking behaviors. The results showed that concrete early cracking area was decreased first and then increased, while early cracking area was the smallest, as sand ratio of C30 and C50 were separately 44% and 41%. The C30 compressive strength was continuously increasing, and compressive strength of C50 first increased and then dropped.
引用
收藏
页码：39 / 44
页数：6
相关论文
共 50 条
  • [11] Early-Age Cracking in Concrete: Causes, Consequences, Remedial Measures, and Recommendations
    Safiuddin, Md.
    Kaish, A. B. M. Amrul
    Woon, Chin-Ong
    Raman, Sudharshan N.
    APPLIED SCIENCES-BASEL, 2018, 8 (10):
  • [12] Quantification of effects of fly ash type on concrete early-age cracking
    Riding, Kyle A.
    Poole, Jonathan L.
    Schindler, Anton K.
    Juenger, Maria C. G.
    Folliard, Kevin J.
    ACI MATERIALS JOURNAL, 2008, 105 (02) : 149 - 155
  • [13] Tensile creep and early-age concrete cracking due to restrained shrinkage
    Khan, Inamullah
    Castel, Arnaud
    Gilbert, Raymond Ian
    CONSTRUCTION AND BUILDING MATERIALS, 2017, 149 : 705 - 715
  • [14] Shrinkage-cracking behavior of OPC-fiber concrete at early-age
    Tarek Aly
    Jay G. Sanjayan
    Materials and Structures, 2010, 43 : 755 - 764
  • [15] Early-Age Cracking of Self-Consolidating Concrete with Lightweight and Normal Aggregates
    Radlinska, Aleksandra
    Kaszynska, Maria
    Zielinski, Adam
    Ye, Hailong
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2018, 30 (10)
  • [16] Effect of crystalline admixture on early-age residual stress and cracking potential of high-strength concrete
    Feng, Zhizhuo
    Shen, Dejian
    Zhang, Jingbin
    Tang, Hui
    Jiang, Guoqing
    STRUCTURAL CONCRETE, 2023, 24 (03) : 4243 - 4258
  • [17] Shrinkage-cracking behavior of OPC-fiber concrete at early-age
    Aly, Tarek
    Sanjayan, Jay G.
    MATERIALS AND STRUCTURES, 2010, 43 (06) : 755 - 764
  • [18] Analysis of the early-age cracking in concrete made from rapid hardening cement
    Cifuentes, Hector
    Karihaloo, Bhushan L.
    HORMIGON Y ACERO, 2018, 69 (285): : 101 - 112
  • [19] Chloride Diffusivity of High-Performance Concrete due to Early-Age Shrinkage Cracking
    Li-Na Ma
    Yan-Hua Zhao
    Jin-Xin Gong
    KSCE Journal of Civil Engineering, 2019, 23 : 5173 - 5182
  • [20] Prediction of early-age cracking of fiber-reinforced concrete due to restrained shrinkage
    Kwon, Seung Hee
    Shah, Surendra P.
    ACI MATERIALS JOURNAL, 2008, 105 (04) : 381 - 389
12345