Fatigue Crack Initiation Mechanism for Cast 319-T7 Aluminum Alloy

被引：14
作者：
Jang, Younghwan [1 ]
Jin, Sanguk [2 ]
Jeong, Youin [1 ]
Kim, Sangshik [2 ]
机构：
[1] Korea Aerosp Ind Ltd, Div Res & Dev, Sachon 664942, South Korea
[2] Gyeongsang Natl Univ, I Cube Ctr, Engn Res Ctr, Sch Nano & Adv Mat Engn, Chinju 660701, South Korea
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2009年 / 40A卷 / 07期
关键词：
DEFECTS; PERFORMANCE; PREDICTION; AL-7SI-MG; STRENGTH; BEHAVIOR; POROSITY;
D O I：
10.1007/s11661-009-9834-0
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, the fatigue crack initiation behavior of cast 319-T7 aluminum alloy at 25 A degrees C and 150 A degrees C was examined based on detailed scanning electron microscopy (SEM) fractographic analysis. The stress-life (S-N) type, uniaxial fatigue tests were conducted for the 319-T7 specimen at a stress ratio (R) of -1 and at 25 A degrees C and 150 A degrees C, and the fractographs of all the fatigued specimens were documented using SEM. At 25 A degrees C, all the fatigue cracks for the specimens initiated from porosity located at or near the specimen surface. At 150 A degrees C, the fatigue crack initiation occurred at porosities near surface for 11 out of 29 specimens. For those specimens with relatively small or no porosities near surface and fatigued at 150 A degrees C, the fatigue crack initiation by slip band mechanism tended to occur and coarse transgranular facets were observed. The oxide film was often observed on the coarse transgranular facet for the those specimens using the slip band mechanism. The fatigue crack initiation mechanism for cast 319-T7 alloy at 25 A degrees C and 150 A degrees C was proposed based on extensive fractographic analysis results.
引用
收藏
页码：1579 / 1587
页数：9
相关论文
共 50 条
[21]   The behavior of fatigue crack initiation and propagation in AA2524-T34 alloy [J].
Zheng, Z. Q. ;
Cai, B. ;
Zhai, T. ;
Li, S. C. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (4-5) :2017-2022
[22]   Fatigue life prediction of cast aluminum alloy based on porosity characteristics [J].
Nourian-Avval, Ahmad ;
Fatemi, Ali .
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2020, 109
[23]   Fatigue Property and Small Crack Propagation Mechanism of MIG Welding Joint of 6005A-T6 Aluminum Alloy [J].
Peng, Zeng ;
Yang, Shanglei ;
Wang, Zhentao ;
Gao, Zihao .
MATERIALS, 2022, 15 (13)
[24]   Effect of temperature on the tensile properties of an as-cast aluminum alloy A319 [J].
Rincon, E. ;
Lopez, H. F. ;
Cisneros, M. M. ;
Mancha, H. ;
Cisneros, M. A. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 452 :682-687
[25]   The Effect of Structural Quality on Fatigue Life in 319 Aluminum Alloy Castings [J].
Ozdes, Huseyin ;
Tiryakioglu, Murat .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (02) :736-743
[26]   A study of small fatigue crack growth in cast aluminum and prediction of fatigue properties [J].
Caton, MJ ;
Jones, JW ;
Allison, JE .
SMALL FATIGUE CRACKS: MECHANICS, MECHANISMS, AND APPLICATIONS, 1999, :155-166
[27]   Explore the mechanism of high fatigue crack propagation rate in fine microstructure of friction stir welded aluminum alloy [J].
Dai, Qilei ;
Liang, Zhifang ;
Chen, Gaoqiang ;
Meng, Lichun ;
Shi, Qingyu .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 580 :184-190
[28]   Influence of casting defects on fatigue crack initiation and fatigue limit of ductile cast iron [J].
Collini, L. ;
Pirondi, A. ;
Bianchi, R. ;
Cova, M. ;
Milella, P. P. .
11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10
[29]   Effects of shot peening with different coverage on surface integrity and fatigue crack growth properties of 7B50-T7751 aluminum alloy [J].
Qin, Zhi ;
Li, Bin ;
Zhang, Han ;
Wilfried, Tiako Youani Andre ;
Gao, Tao ;
Xue, Hongqian .
ENGINEERING FAILURE ANALYSIS, 2022, 133
[30]   Influence of Pore Size and Crystallography on the Small Crack HCF Behavior of an A357-T6 Cast Aluminum Alloy [J].
Serrano-Munoz, I. ;
Dancette, S. ;
Verdu, C. ;
Buffiere, J. -Y. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2020, 51 (03) :1416-1427
12345