Microstructure evolution and degradation mechanisms of reactor internal steel irradiated with heavy ions

被引：13

作者：

Borodin, O. V. ^{[1
]}

Bryk, V. V. ^{[1
]}

Kalchenko, A. S. ^{[1
]}

Parkhomenko, A. A. ^{[1
]}

Shilyaev, B. A. ^{[1
]}

Tolstolutskaya, G. D. ^{[1
]}

Voyevodin, V. N. ^{[1
]}

机构：

[1] Kharkov Phys & Technol Inst, Ctr Nat Sci, Inst Solid State Phys Mat & Technol, UA-61108 Kharkov, Ukraine

来源：

JOURNAL OF NUCLEAR MATERIALS | 2009年 / 385卷 / 02期

关键词：

D O I：

10.1016/j.jnucmat.2008.12.007

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Structure evolution and degradation mechanisms during irradiation of 18Cr-10Ni-Ti steel (material of VVER-1000 reactor internals are investigated). Using accelerator irradiations with Cr3+ and Ar+ ions allowed studying effects of dose rate, different initial structure state and implanted ions on features of structure evolution and main mechanisms of degradation including low temperature swelling and embrittlement of the 18Cr-10Ni-Ti steel. It is shown that differences in dose rate at most irradiation temperatures mainly exert their influence on the duration of the swelling transient regime. Calculations of possible transmutation products during irradiation of this steel in a VVER-1000 spectrum were performed. it is shown that gaseous atoms (He and H), which are generated simultaneously with radiation defects, stabilize the elements of radiation microstructure and influence the swelling. The nature of deformation under different temperatures of irradiation and of mechanical testing is investigated. it is shown that the temperature sensitivity of swelling behaviour in the investigated steel, with different initial structures can be connected with the dynamic behaviour of point defect sinks. (C) 2008 Published by Elsevier B.V.

引用

页码：325 / 328

页数：4

共 10 条

[1] A MONTE-CARLO COMPUTER-PROGRAM FOR THE TRANSPORT OF ENERGETIC IONS IN AMORPHOUS TARGETS [J].

BIERSACK, JP ;

HAGGMARK, LG .

NUCLEAR INSTRUMENTS & METHODS, 1980, 174 (1-2) :257-269

[2] Swelling and post-irradiated deformation structures in 18Cr-10Ni-Ti irradiated with heavy ions [J].

Borodin, OV ;

Bryk, VV ;

Kalchenko, AS ;

Neklyudov, IM ;

Parkhomenko, AA ;

Voyevodin, VN .

JOURNAL OF NUCLEAR MATERIALS, 2004, 329 :630-633

[3]

GARNER FA, 1993, PROCEEDINGS OF THE SIXTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS - WATER REACTORS, P783

[4]

GARNER FA, 1994, MAT SCI TECHNOL A, V10, P420

[5] A COMPARISON OF THE GROWTH OF HELIUM AND NEON BUBBLES IN NICKEL [J].