Electrical Characterization of Thermally Activated Defects in n-Type Float-Zone Silicon

Float-zone (FZ) silicon is usually assumed to be bulk defect-lean and stable. However, recent studies have revealed that detrimental defects can be thermally activated in FZ silicon wafers and lead to a reduction of carrier lifetime by up to two orders of magnitude. A robust methodology which combines different characterization techniques and passivation schemes is used to provide new insight into the origin of degradation of 1 omega center dot cm n-type phosphorus doped FZ silicon (with nitrogen doping during growth) after annealing at 500 degrees C. Carrier lifetime and photoluminescence experiments are first performed with temporary room temperature surface passivation which minimizes lifetime changes which can occur during passivation processes involving thermal treatments. Temperature- and injection-dependent lifetime spectroscopy is then performed with a more stable passivation scheme, with the same samples finally being studied by deep level transient spectroscopy (DLTS). Although five defect levels are found with DLTS, detailed analysis of injection-dependent lifetime data reveals that the most detrimental defect levels could arise from just two independent single-level defects or from one two-level defect. The defect parameters for these two possible scenarios are extracted and discussed.