Cavitation erosion of plasma-sprayed NiTi coatings

被引：64
作者：
Stella, J
Schüller, E
Hessing, C
Hamed, OA
Pohl, M
Stöver, D
机构：
[1] Ruhr Univ Bochum, Inst Werkstoffe, D-44780 Bochum, Germany
[2] Forschungszentrum Julich, IWV 1, D-52425 Julich, Germany
来源：
WEAR | 2006年 / 260卷 / 9-10期
关键词：
cavitation erosion; NiTi; plasma; coatings;
D O I：
10.1016/j.wear.2005.06.002
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Ni-Ti protective layers are under development to increase the cavitation resistance of materials such as stainless steel. For the present work, layers were obtained by vacuum plasma spraying (VPS) from both elemental powder mixtures and pre-alloyed powder. Characterization was done with respect to phase formation and impurity content. Cavitation erosion resistance was examined using a standard ultrasonic cavitation test. In the coating from the pre-alloyed powder, a higher resistance due to the lower presence of non-shape memory phases was observed. The cavitation erosion resistance of pre-alloyed plasma-sprayed layers is in good agreement with the one of pore-free NiTi samples evaluated in this study and others described in the literature. (c) 2005 Elsevier B.V. All rights reserved.
引用
收藏
页码：1020 / 1027
页数：8
相关论文
共 20 条
[1]  
*ASTM, 1998, G3298 ASTM, P6
[2]   Vacuum plasma spraying of NiTi protection layers [J].
Bram, M ;
Ahmad-Khanlou, A ;
Buchkremer, HP ;
Stöver, D .
MATERIALS LETTERS, 2002, 57 (03) :647-651
[3]   Cavitation erosion resistance of heat-treated NiTi [J].
Cheng, FT ;
Shi, P ;
Man, HC .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 339 (1-2) :312-317
[4]  
CLAYTON O, 1993, WEAR, V162, P202
[5]   Cavitation erosion-corrosion characteristics of laser surface modified NiTi shape memory alloy [J].
Cui, ZD ;
Man, HC ;
Cheng, FT ;
Yue, TM .
SURFACE & COATINGS TECHNOLOGY, 2003, 162 (2-3) :147-153
[6]   Plastic deformation behaviour in Ni3Ti single crystals with D024 structure [J].
Hagihara, K ;
Nakano, T ;
Umakoshi, Y .
ACTA MATERIALIA, 2003, 51 (09) :2623-2637
[7]   Cavitation-resistant TiNi films deposited by using cathodic are plasma ion plating [J].
He, JL ;
Won, KW ;
Chang, CT ;
Chen, KC ;
Lin, HC .
WEAR, 1999, 233 :104-110
[8]   Fabrication of NiTi intermetallic compound coating made by laser plasma hybrid spraying of mechanically alloyed powders [J].
Hiraga, H ;
Inoue, T ;
Kamado, S ;
Kojima, Y ;
Matsunawa, A ;
Shimura, H .
SURFACE & COATINGS TECHNOLOGY, 2001, 139 (01) :93-100
[9]   Effect of laser irradiation condition on bonding strength in laser plasma hybrid spraying [J].
Hiraga, H ;
Inoue, T ;
Matsunawa, A ;
Shimura, H .
SURFACE & COATINGS TECHNOLOGY, 2001, 138 (2-3) :284-290
[10]   Cavitation erosion mechanism of NiTi coatings made by laser plasma hybrid spraying [J].
Hiraga, H ;
Inoue, T ;
Shimura, H ;
Matsunawa, A .
WEAR, 1999, 231 (02) :272-278
12