Isothermal Crystallization Behavior of Poly(L-lactic acid)/Organo-Montmorillonite Composites

被引：0
|
作者：
Cai, Yan-Hua [1 ]
Miao, Ya-Wei [1 ]
Wang, Zheng-Yong [1 ]
机构：
[1] Chongqing Univ Arts & Sci, Chongqing Key Lab Environm Mat & Remediat Technol, Chongqing 402160, Peoples R China
来源：
ASIAN JOURNAL OF CHEMISTRY | 2014年 / 26卷 / 04期
基金：
中国博士后科学基金;
关键词：
Montmorillonite; Crystallization time; Poly(L-lactic acid); Crystallization kinetic; MICROSTRUCTURE; NANOCOMPOSITES; KINETICS; HYBRID; ACID); CLAY;
D O I：
10.14233/ajchem.2014.16423
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
In this research, organo-montmorillonite (OMMT) was synthesized by ion exchange technology, Then the poly(L-lactic acid)(PLLA)/OMMT composites were fabricated using melt blending and hot-press forming. The isothermal crystallization behavior of PLLA/OMMT composites was investigated in detail and isothermal crystllization behavior was affected by crystallization temperature and organomontmorillonite content. Compared to the neat poly(L-lactic acid), the half-time of poly(L-lactic acid) with 5 % organo-montmorillonite decreases from 2991.5s to 327s. and the kinetic of isothermal crystallization of PLLA/OMMT was described by Avrami theory and the results showed that PLLA/OMMT composite had complicated nucleation mechanism.
引用
收藏
页码：1237 / 1240
页数：4
相关论文
共 50 条
  • [21] Isothermal and non-isothermal crystallization behavior of poly(L-lactic acid): Effects of stereocomplex as nucleating agent
    Tsuji, Hideto
    Takai, Hiroki
    Saha, Swapan Kumar
    POLYMER, 2006, 47 (11) : 3826 - 3837
  • [22] Isothermal and non-isothermal crystallization behavior of poly(L-lactic acid): Effects of stereocomplex as nucleating agent
    Tsuji, Hideto
    Takai, Hiroki
    Saha, Swapan Kumar
    POLYMER, 2006, 47 (15) : 5430 - 5430
  • [23] Influence of Stretching on Crystallization Behavior of Poly (L-lactic acid)
    Xing Qian
    Zhang Xiu-Qin
    Luo Fa-Liang
    Liu Guo-Ming
    Wang Du-Jin
    CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2011, 32 (04): : 971 - 977
  • [24] Characterization of organo-montmorillonite (OMMT) modified wood flour and properties of its composites with poly(lactic acid)
    Liu, Ru
    Luo, Shupin
    Cao, Jinzhen
    Peng, Yao
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2013, 51 : 33 - 42
  • [25] Organo-montmorillonite modified wood flour/poly (lactic acid) composites via different modification process
    Wang, Zhiping
    Wang, Chen
    Qin, Ye
    Huang, Anmin
    Liu, Ru
    POLYMER COMPOSITES, 2021, 42 (02) : 987 - 994
  • [26] Properties of Poly(Lactic Acid)/Organo-Montmorillonite Nanocomposites Prepared by Solution Intercalation
    Li, Yang
    Ren, Peng-Gang
    Zhang, Qian
    Shen, Ting-Ting
    Ci, Ji-Hao
    Fang, Chang-Qing
    JOURNAL OF MACROMOLECULAR SCIENCE PART B-PHYSICS, 2013, 52 (08): : 1041 - 1055
  • [27] Isothermal and Non-Isothermal Crystallization of Poly(L-lactic acid)/Poly(butylene terephthalate) Blends
    Di Lorenzo, Maria Laura
    Rubino, Paolo
    Cocca, Mariacristina
    JOURNAL OF APPLIED POLYMER SCIENCE, 2014, 131 (12)
  • [28] Flexural, morphological and thermal properties of poly(lactic acid)/organo-montmorillonite nanocomposites
    Shyang, Chow Wen
    Kuen, Lok Sook
    POLYMERS & POLYMER COMPOSITES, 2008, 16 (04): : 263 - 270
  • [29] Effect of a Novel Nucleating Agent on Isothermal Crystallization of Poly(L-lactic acid)
    Wen Liang
    Xin Zhong
    CHINESE JOURNAL OF CHEMICAL ENGINEERING, 2010, 18 (06) : 899 - 904
  • [30] Crystallization behavior of plasticized poly(lactide) film by poly(l-lactic acid)-poly(ethylene glycol)-poly(l-lactic acid) triblock copolymer
    Jariyasakoolroj, Piyawanee
    Rojanaton, Nattapon
    Jarupan, Lerpong
    POLYMER BULLETIN, 2020, 77 (05) : 2309 - 2323
12345