Implantation of P ions in SiO2 layers with embedded Si nanocrystals

The effect of 10(13)-10(16) cm(-2) P ions implantation and of subsequent annealing on Si nanocrystals (Si-ncs), formed preliminarily in SiO2 layers by the ion-beam synthesis, has been studied. Photoluminescence (PL), Raman spectroscopy, high resolution electron microscopy (HREM), X-Ray Photoelectron Spectroscopy (XPS) and optical absorption were used for characterizations. The low fluence implantations have shown even individual displacements in Si-ncs quench their PL. Restoration of PL from partly damaged Si-ncs proceeds at annealing less than 1000 degreesC. In the low fluence implanted and annealed samples an increased Si-ncs PL has been found and ascribed to the radiation-induced shock crystallization of stressed Si nanoprecipitates. Annealing at temperatures under 1000 degreesC are inefficient when P ion fluences exceed 1014 cm(-2), thus becoming capable to amorphize Si-ncs. High crystallization temperature of the amorphized Si-ncs is attributed to a counteraction of their shell layers. After implantation of the highest P fluences an enhanced recovery of PL was found from P concentration over 0.1 at.%. Raman spectroscopy and HREM showed an increased Si-ncs number in such layers. The effect resembles the impurity-enhanced crystallization, known for heavily doped bulk Si. This effect, along with the data obtained by XPS, is considered as an indication P atoms are really present inside the Si-ncs. However, no evidence of free electrons appearance has been observed. The fact is explained by an increased interaction of electrons with the donor nuclei in Si-ncs. (C) 2004 Elsevier B.V. All rights reserved.