Microstructure evolution associated with adiabatic shear bands and shear band failure in ballistic plug formation in Ti-6Al-4V targets

被引:125
作者
Murr, L. E. [1 ]
Ramirez, A. C. [1 ]
Gaytan, S. M. [1 ]
Lopez, M. I. [1 ]
Martinez, E. Y. [1 ]
Hernandez, D. H. [1 ]
Martinez, E. [1 ]
机构
[1] Univ Texas El Paso, Dept Met & Mat Engn, El Paso, TX 79968 USA
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2009年 / 516卷 / 1-2期
关键词
Ballistic plugging; Adiabatic shear bands; DRX; Microstructure evolution; Optical and electron metallography; DYNAMIC RECRYSTALLIZATION; PLASTIC-DEFORMATION; HIGH-STRAIN; LOCALIZATION; TITANIUM; DISSIPATION; ALLOYS; STEEL;
D O I
10.1016/j.msea.2009.03.051
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The microstructures and microstructure evolution associated with adiabatic shear band (ASB) formation in ballistic plugging in thick (2.5 cm) Ti-6Al-4V targets impacted by cylindrical, 4340 steel projectiles (2.0 cm in height) at impact velocities ranging from 633 m/s to 1027 m/s (just above the ballistic limit) were investigated by optical and transmission electron microscopy. ASB width increased from 10 mu m to 21 mu m as the velocity increased. ASB evolution was accompanied by the evolution of dark deformation bands composed of alpha' martensite platelets which increased in density with increasing impact velocity. The corresponding Vickers microindentation hardness also increased from HV 619 to HV 632 in contrast to the surrounding matrix microindentation hardness of HV 555. These deformation bands were not necessarily precursors to ASB formation. The ASB average Vickers microindentation hardness was essentially constant at HV 645, a 16% increase over the matrix. This constant microindentation hardness was characterized by a consistent DRX grain structure which varied from equiaxed, defect-free grains (similar to 2 mu m diameter) to heavily dislocated, equiaxed grains. Cracks nucleating and propagating within the ABSs were observed to increase from 8% to 87% of the ASB length with increasing impact velocity. (c) 2009 Elsevier B.V. All rights reserved.
引用
收藏
页码:205 / 216
页数:12
相关论文
共 39 条
[21]   Collective behavior and spacing of adiabatic shear bands [J].
Molinari, A .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1997, 45 (09) :1551-1575
[22]  
MOSS GL, 1980, SHOCK WAVES HIGH STR, P299
[23]   Dynamic recrystallization:: The dynamic deformation regime [J].
Murr, L. E. ;
Pizana, C. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2007, 38A (11) :2611-2628
[24]  
MURR LE, 1982, INT J FRACTURE, V20, P177
[25]  
Nesterenko VF, 1995, METALLURGICAL AND MATERIALS APPLICATIONS OF SHOCK-WAVE AND HIGH-STRAIN-RATE PHENOMENA, P397
[26]   ADIABATIC PLASTIC-DEFORMATION [J].
ROGERS, HC .
ANNUAL REVIEW OF MATERIALS SCIENCE, 1979, 9 :283-311
[27]   A failure criterion based on material instability [J].
Schoenfeld, SE ;
Wright, TW .
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2003, 40 (12) :3021-3037
[28]  
SILLING SA, 1993, 922692 SAND SAND NAT
[29]  
SILLING SA, 2002, CTH REFERENCE UNPUB
[30]   ADIABATIC SHEAR OF TITANIUM AND POLYMETHYLMETHACRYLATE [J].
WINTER, RE .
PHILOSOPHICAL MAGAZINE, 1975, 31 (04) :765-773