Heat fluxes at metal-mold interface during casting solidification

被引：0
作者：
Sabau, Adrian S. [1 ]
机构：
[1] Oak Ridge Natl Lab, Div Met & Ceram, Oak Ridge, TN 37831 USA
来源：
LIGHT METALS 2006 VOL 4: CAST SHOP TECHNOLOGY AND RECYCLING - ALUMINUM | 2006年
关键词：
heat flux; heat transfer coefficient; sensor; inverse heat transfer analysis; casting; solidification;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
In this paper, the heat transfer at the metal-mold interfaces is investigated using a sensor for the direct measurement of heat flux. Casting experiments were conducted using graphite molds for aluminum alloy A356. Several casting experiments were performed using a graphite coating and a boron nitride coating. The temperature of the mold surface was provided by the HFS while the temperature of the casting surface was measured using a thermocouple. Results for the heat transfer coefficients were obtained based on measured heat flux and temperatures. Four stages were clearly identified for the variation in time of the heat flux. Values of the heat transfer coefficient were in good agreement with data from previous studies.
引用
收藏
页码：827 / 832
页数：6
相关论文
共 50 条
  • [31] Non-uniform heat transfer behavior during shell solidification in a wide and thick slab continuous casting mold
    Zhao-zhen Cai
    Miao-yong Zhu
    [J]. International Journal of Minerals, Metallurgy, and Materials, 2014, 21 : 240 - 250
  • [32] Use of experiment and an inverse method to study interface heat transfer during solidification in the investment casting process
    O'Mahoney, D
    Browne, DJ
    [J]. EXPERIMENTAL THERMAL AND FLUID SCIENCE, 2000, 22 (3-4) : 111 - 122
  • [33] Heat transfer at the casting/chill interface during solidification of commercially pure Zn and Zn base alloy (ZA8)
    Ramesh, G.
    Prabhu, K. N.
    [J]. INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2012, 25 (03) : 160 - 164
  • [34] Radiative Heat Transfer Behavior of Mold Fluxes for Casting Low and Medium Carbon Steels
    Wang, Wanlin
    Gu, Kezhuan
    Zhou, Lejun
    Ma, Fanjun
    Sohn, Il
    Min, Dong Joon
    Matsuura, Hiroyuki
    Tsukihashi, Fumitaka
    [J]. ISIJ INTERNATIONAL, 2011, 51 (11) : 1838 - 1845
  • [35] Non-uniform heat transfer behavior during shell solidification in a wide and thick slab continuous casting mold
    Cai, Zhao-zhen
    Zhu, Miao-yong
    [J]. INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2014, 21 (03) : 240 - 250
  • [36] Radiative Heat Transfer in Transition Metal Oxides contained in Mold Fluxes
    Diao, Jiang
    Xie, Bing
    Xiao, Jianping
    Ji, Chengqing
    [J]. ISIJ INTERNATIONAL, 2009, 49 (11) : 1710 - 1714
  • [37] Influence of Mold Flux on Initial Solidification of Hypo-Peritectic Steel in A Continuous Casting Mold
    Hanao, Masahito
    Kawamoto, Masayuki
    Yamanaka, Akihiro
    [J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2014, 100 (04): : 581 - 590
  • [38] Influence of Mold Flux on Initial Solidification of Hypo-Peritectic Steel in a Continuous Casting Mold
    Hanao, Masahito
    Kawamoto, Masayuki
    Yamanaka, Akihiro
    [J]. ISIJ INTERNATIONAL, 2012, 52 (07) : 1310 - 1319
  • [39] Determination of interface heat transfer coefficient between aluminum casting and graphite mold
    V. E. Bazhenov
    A. V. Koltygin
    Yu. V. Tselovalnik
    A. V. Sannikov
    [J]. Russian Journal of Non-Ferrous Metals, 2017, 58 : 114 - 123
  • [40] Determination of interface heat transfer coefficient between aluminum casting and graphite mold
    Bazhenov, V. E.
    Koltygin, A. V.
    Tselovalnik, Yu. V.
    Sannikov, A. V.
    [J]. RUSSIAN JOURNAL OF NON-FERROUS METALS, 2017, 58 (02) : 114 - 123
12345