Domain Size Manipulation of Perflouorinated Polymer Electrolytes by Sulfonic Acid-Functionalized MWCNTs To Enhance Fuel Cell Performance

被引:82
作者
Kannan, Ramaiyan [1 ]
Parthasarathy, Meera [1 ]
Maraveedu, Sreekuttan U. [1 ]
Kurungot, Sreekumar [1 ]
Pillai, Vijayamohanan K. [1 ]
机构
[1] Natl Chem Lab, Phys & Mat Chem Div, Pune 411008, Maharashtra, India
关键词
NANOCOMPOSITE MEMBRANE; COMPOSITE MEMBRANES; NAFION; TRANSPORT; COPOLYMERS; HYDROGEN; AIR;
D O I
10.1021/la9005218
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
The application of sulfonic acid-functionalized multiwalled (s-MWNT) carbon nanotubes to manipulate the hydrophilic domain size of Nafion membranes is explored here as an option for tuning the proton conductivity of polymer electrolyte membranes for hydrogen-oxygen fuel cells. The electrochemical impedance experiments provide preliminary evidence of increased proton conductivity, while small-angle X-ray scattering measurements line. out enhanced ionic cluster domain size in these composite membranes as the central reason for higher conductivity (70 angstrom for the optimum composite membrane vs 50 angstrom for Nafion 115) values. Scanning electrochemical microscopy indicates synergistic interaction between the sulfonic acid functional groups present in the Nation membrane and those on the nanotube surface. More interestingly, the nanotube-tailored Nafion membranes ameliorate the performance of fuel cells as confirmed by measurements at a sin le-cell level, which reveal a maximum power density of 380 mW cm(-2), higher than those of Nafion 115 (250 mW cm(-2)) and recast Nafion (230 mW cm-2) membranes. Thus, in addition to providing an elegant means of controlling the ionic cluster size, the strategic approach of using CNT both as an anchoring backbone for -SO3H groups to enrich proton conductivity and as a blending agent to improve the mechanical characteristics of the Nafion phase might be helpful in alleviating many critical problems associated with the use of commercial Nafion membranes.
引用
收藏
页码:8299 / 8305
页数:7
相关论文
共 37 条
[31]   Direct polymerization of sulfonated poly(arylene ether sulfone) random (statistical) copolymers: candidates for new proton exchange membranes [J].
Wang, F ;
Hickner, M ;
Kim, YS ;
Zawodzinski, TA ;
McGrath, JE .
JOURNAL OF MEMBRANE SCIENCE, 2002, 197 (1-2) :231-242
[32]   Rapidly functionalized, water-dispersed carbon nanotubes at high concentration [J].
Wang, YB ;
Iqbal, Z ;
Mitra, S .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2006, 128 (01) :95-99
[33]   Polymer electrolyte membranes incorporated with nanometer-size particles of Pt and/or metal-oxides: Experimental analysis of the self-humidification and suppression of gas-crossover in fuel cells [J].
Watanabe, M ;
Uchida, H ;
Emori, M .
JOURNAL OF PHYSICAL CHEMISTRY B, 1998, 102 (17) :3129-3137
[34]   Assessment of the electrochemical behavior of two-dimensional networks of single-walled carbon nanotubes [J].
Wilson, Neil R. ;
Guille, Manon ;
Dumitrescu, Ioana ;
Fernandez, Virginia R. ;
Rudd, Nicola C. ;
Williams, Cara G. ;
Unwin, Patrick R. ;
Macpherson, Julie V. .
ANALYTICAL CHEMISTRY, 2006, 78 (19) :7006-7015
[35]   Preparation and characterization of sulfated zirconia(SO42-/ZrO2)/Nafion composite membranes for PEMFC operation at high temperature/low humidity [J].
Zhai, Yunfeng ;
Zhang, Huamin ;
Hu, Jingwei ;
Yi, Baolian .
JOURNAL OF MEMBRANE SCIENCE, 2006, 280 (1-2) :148-155
[36]   Exfoliated Pt-clay/Nafion nanocomposite membrane for self-humidifying polymer electrolyte fuel cells [J].
Zhang, Wenjing ;
Li, Martin Ka Shing ;
Yue, Po-Lock ;
Gao, Ping .
LANGMUIR, 2008, 24 (06) :2663-2670
[37]  
1998, NAE302