Manufacturing process of dispersed intermetallic compounds Al alloy composites by using porous nickel

被引:9
作者
Choi, Y. B. [1 ]
Matsugi, K. [1 ]
Sasaki, G. [1 ]
机构
[1] Hiroshima Univ, Grad Sch Engn, Higashihiroshima 7398527, Japan
关键词
Porous; nickel; intermetallic; compound; Al3Ni; manufacturing; process;
D O I
10.1177/0021998313497496
中图分类号
TB33 [复合材料];
学科分类号
摘要
A new process is proposed to fabricate an intermetallic compound-reinforced aluminum alloy matrix composite using the reaction between porous nickel and molten aluminum alloy. The intermetallic compound-reinforced aluminum alloy composite was manufactured with the infiltration process method. Porous nickel reacted with the molten aluminum alloy at 973 K, and the intermetallic compound of Al3Ni was generated on the surface of the porous nickel. The generated intermetallic compound Al3Ni is delaminated due to different thermal expansion coefficient with nickel and moves in the direction of aluminum matrix. The effects of processing variables such as specific surface area of porous nickel, holding time after infiltrated molten aluminum alloy, and cooling rate on the formation and dispersion behavior of Al3Ni were investigated.
引用
收藏
页码:2289 / 2295
页数:7
相关论文
共 8 条
[1]  
[Anonymous], KEY ENG MAT
[2]  
Choi YB, 2013, MATER TRANS, V54, P595, DOI [10.2320/matertrans.MBW201214, 10.2320/matertrans.MBW2012141]
[3]   Production and wear characterisation of AA 6061 matrix titanium carbide particulate reinforced composite by enhanced stir casting method [J].
Gopalakrishnan, S. ;
Murugan, N. .
COMPOSITES PART B-ENGINEERING, 2012, 43 (02) :302-308
[5]  
Kubaschewski O, MAT THERMOCHEMISTRY, P258
[6]   Fabrication of Al/Al2O3 composites by in-situ powder metallurgy (IPM) [J].
Pournaderi, S. ;
Mahdavi, S. ;
Akhlaghi, F. .
POWDER TECHNOLOGY, 2012, 229 :276-284
[7]  
Yamaguchi T., 1991, 911284 SAE
[8]  
[No title captured]