Orientation-dependent nanoscratch resistance of zirconium diboride ceramic grains

The orientation dependence of scratch resistance of zirconium diboride (ZrB2) grains was investigated during nanoscratch testing. The experimental material was produced by spark plasma sintering (SPS) and the crystal orientation of ZrB2 grains was determined by electron backscatter diffraction (EBSD) technique. Scratches were prepared on a previously mapped surface area by an instrumented indentation machine using Berkovich tip with constant loads of 50, 100 and 150 mN along lengths of 200 mu m. The generated surface topography was studied by scanning electron microscopy (SEM), confocal and atomic force microscopy (AFM). Micro-plasticity was observed in the form of slip-lines and microcradcing along the scratch tracks. The analysis of experimental data revealed significant anisotropy in residual scratch depth with the lowest resistance corresponding to the tilt angle of around phi = 50 degrees-60 degrees.Anisotropic crack initiation was observed, which depends on the load and crystal orientation. The orientation dependence of scratch resistance showed a proportional tendency with hardness, yield and rupture stress anisotropies reported recently by the present authors. (C) 2016 Elsevier Ltd. All rights reserved.