Coupling of superduplex stainless steel and cast nickel-aluminium bronze in sea water

被引：5
|
作者：
Francis, R [1 ]
机构：
[1] Weir Mat & Foundries, Pk Works, Manchester M40 2BA, Lancs, England
来源：
BRITISH CORROSION JOURNAL | 1999年 / 34卷 / 02期
关键词：
D O I：
10.1179/000705999101500789
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Tests have been performed at about 25 degrees C in both natural and chlorinated sea waters on couples of nickel-alminium bronze (NAB) and Zeron 100 (Z100) superduplex stainless steel. Two NAB/Z100 area ratios (1 : 1 and 1 : 10) were used in exposures of 60 days. The results in natural sea water showed severe localised corrosion of NAB both in the crevices and on open surfaces at both area ratios. In chlorinated sea water there was no corrosion at a 1 : 1 area ratio. The attack is explained in terms of the different cathodic reactions occurring in natural and chlorinated sea waters, and the metallurgical structure of: NAB. Service experiences with couples of NAB and superduplex stainless steel are described and recommendations are given for the avoidance of problems.
引用
收藏
页码：139 / 144
页数：6
相关论文
共 50 条
  • [1] The corrosion of nickel-aluminium bronze in seawater
    Wharton, JA
    Barik, RC
    Kear, G
    Wood, RJK
    Stokes, KR
    Walsh, FC
    CORROSION SCIENCE, 2005, 47 (12) : 3336 - 3367
  • [2] Erosion and erosion-corrosion performance of cast and thermally sprayed nickel-aluminium bronze
    Barik, RC
    Wharton, JA
    Wood, RJK
    Tan, KS
    Stokes, KR
    WEAR, 2005, 259 (1-6) : 230 - 242
  • [3] Structure of oxide bifilms in nickel-aluminium bronze alloys
    Song, Heqian
    Zhang, Lunyong
    Cao, Fuyang
    Shen, Hongxian
    Ning, Zhiliang
    Huang, Yongjiang
    Zhao, Xinyi
    Gu, Xu
    li, Lu
    Sun, Jianfei
    APPLIED SURFACE SCIENCE, 2021, 541
  • [4] Role of second phases in the stress corrosion cracking of a nickel-aluminium bronze in saline water
    Fonlupt, S
    Bayle, B
    Delafosse, D
    Heuze, JL
    CORROSION SCIENCE, 2005, 47 (11) : 2792 - 2806
  • [5] Unusual corrosion of nickel-aluminium bronze in a hydroelectric power plant
    Linhardt, P.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2015, 66 (12): : 1536 - 1541
  • [6] An unusual failure of a nickel-aluminium bronze (NAB) hydraulic valve
    Byrnes, R. T.
    Lynch, S. P.
    ENGINEERING FAILURE ANALYSIS, 2015, 49 : 122 - 136
  • [7] Morphology and fracture of oxide bifilm defects in nickel-aluminium bronze
    Song, Heqian
    Zhang, Lunyong
    Shen, Hongxian
    Cao, Fuyang
    Zhao, Xinyi
    Gu, Xu
    Jin, Zhishuai
    Sun, Jianfei
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 10 : 926 - 934
  • [8] Premature failure of superduplex stainless steel pipe by pitting in sea water environment
    Smiderle, J.
    Pardal, J. M.
    Tavares, S. S. M.
    Vidal, A. C. N.
    ENGINEERING FAILURE ANALYSIS, 2014, 46 : 134 - 139
  • [9] CLADDING OF STAINLESS STEEL WITH ALUMINIUM BRONZE
    JORDAN, DE
    AUCHTERL.AJ
    HEATH, DJ
    METAL CONSTRUCTION AND BRITISH WELDING JOURNAL, 1969, 1 (12SI): : 11 - &
  • [10] Force prediction models for helical end milling of nickel-aluminium bronze
    Zhou, Ruihu
    Yang, Wenyu
    Yang, Kun
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2016, 86 (5-8): : 1487 - 1498
12345