Bifurcation of the Kirkendall plane during interdiffusion in the intermetallic compound β-NiAl

被引:49
作者
Paul, A [1 ]
Kodentsov, AA [1 ]
van Loo, FJJ [1 ]
机构
[1] Eindhoven Univ Technol, Lab Solid State & Mat Chem, NL-5600 MB Eindhoven, Netherlands
关键词
diffusion; Kirkendall plane; intermetallic compounds; NiAl;
D O I
10.1016/j.actamat.2004.05.028
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
An experimental verification of the phenomenological approach introduced earlier [Phys. Rev. Lett. 86 (2001) 3352] to rationalize possible bifurcation of the Kirkendall plane inside a diffusion-grown compound layer is presented. A reaction couple, in which a single-phased layer of beta-NiAl intermetallic is growing during interdiffusion from its adjacent phases is used as a model system. The corresponding Kirkendall velocity diagram was constructed on the basis of inter- and intrinsic diffusion data obtained with the diffusion couple technique. The agreement between the predicted and experimentally determined position of the marker planes was found to be good within the range of uncertainty of the experimental results, which demonstrates the validity of the proposed model. It is observed that the position of a stable Kirkendall plane is characterized not only by the presence of inert markers, but also by a different crystal morphology at both sides of this plane. The bifurcation of the Kirkendall plane within the product layer of beta-NiAl is directly related to the growth of grains of this phase at a location in between (and not at) the interfaces with starting materials. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:4041 / 4048
页数:8
相关论文
共 26 条
[1]   The anti-structural bridge mechanism for diffusion in ordered alloys of the B2 type [J].
Belova, IV ;
Murch, GE .
INTERMETALLICS, 1998, 6 (02) :115-119
[2]   THERMODYNAMICS AND DEFECT STRUCTURE OF INTERMETALLIC PHASES WITH THE B2 (CSCL) STRUCTURE [J].
CHANG, YA ;
NEUMANN, JP .
PROGRESS IN SOLID STATE CHEMISTRY, 1982, 14 (04) :221-301
[3]  
DARKEN LS, 1948, T AM I MIN MET ENG, V175, P184
[4]   Ni tracer self-diffusion, interdiffusion and diffusion mechanisms in NiAl [J].
Divinski, SV ;
Herzig, C .
DEFECTS AND DIFFUSION IN METALS: AN ANNUAL RETROSPECTIVE IV, 2002, 203-2 :177-192
[5]   Ni tracer diffusion in the B2-compound NiAl:: Influence of temperature and composition [J].
Frank, S ;
Divinski, SV ;
Södervall, U ;
Herzig, C .
ACTA MATERIALIA, 2001, 49 (08) :1399-1411
[6]  
GULPEN JH, 1995, Z METALLKD, V86, P530
[7]   A phenomenological treatment of diffusion in Al-Fe and Al-Ni alloys having B2-BCC ordered structure [J].
Helander, T ;
Ågren, J .
ACTA MATERIALIA, 1999, 47 (04) :1141-1152
[8]  
JANSSEN MMP, 1967, T METALL SOC AIME, V239, P1372
[9]  
JANSSEN MMP, 1973, METALL TRANS, V4, P1623
[10]   ON THE COMPOSITION DEPENDENCIES OF SELF-DIFFUSION COEFFICIENTS IN B2 INTERMETALLIC COMPOUNDS [J].
KAO, CR ;
CHANG, YA .
INTERMETALLICS, 1993, 1 (04) :237-250