Preparation of AlRu intermetallic compounds by mechanical alloying

被引：8
作者：
de Medeiros, S. N.
Machado, F. L. A.
Zampiere, R. B.
Santos, I. A.
Paesano, A., Jr.
机构：
[1] Univ Estadual Maringa, Dept Fis, BR-87020900 Maringa, Parana, Brazil
[2] Univ Fed Pernambuco, Dept Fis, BR-50670901 Recife, PE, Brazil
来源：
JOURNAL OF NON-CRYSTALLINE SOLIDS | 2006年 / 352卷 / 32-35期
关键词：
mechanical alloying; quasicrystals; X-ray diffraction;
D O I：
10.1016/j.jnoncrysol.2006.02.121
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The formation of Al6Ru intermetallic compounds using high-energy ball milling was investigated. High-purity Al and Ru crystalline powders, in the relative (molar) ratio of 6: 1, were milled for periods up to 30 h. Samples of the milled materials were annealed at different times and temperatures. The microstructures of the annealed samples were compared to those of the as-milled samples. It was found that the obtained alloys have compositions that are in accord with the Al-Ru phase diagram. However, the X-ray analysis of a 10 h milled sample, annealed at 873 K for 30 min, showed evidence of the formation of a quasicrystalline icosahedral alloy mixed with the crystalline Al6Ru. Scanning electron microscopy showed that the microstructures are similar to those obtained by other sample preparation techniques. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：3718 / 3720
页数：3
相关论文
共 10 条
[1]   ELECTRICAL TRANSPORT-PROPERTIES OF THE ALUMINUM-RUTHENIUM ICOSAHEDRAL PHASE [J].
ANLAGE, SM ;
JOHNSON, WL ;
COTTS, EJ ;
FOLLSTAEDT, DM ;
KNAPP, JA .
PHYSICAL REVIEW B, 1988, 38 (11) :7802-7805
[2]  
BANCEL PA, 1986, PHYS REV B, V33, P917
[3]   Low temperature magneto-transport properties of the I-AI6Ru quasicrystalline alloy [J].
De Medeiros, SN ;
Machado, FLA ;
Acioli, LH .
FERROELECTRICS, 2004, 305 :193-198
[4]   FORMATION OF QUASICRYSTALS BY MECHANICAL ALLOYING [J].
ECKERT, J ;
SCHULTZ, L ;
URBAN, K .
APPLIED PHYSICS LETTERS, 1989, 55 (02) :117-119
[5]   Measurement of the density of states of a Al6Ru quasicrystalline alloy by ultrafast thermomodulation [J].
Ferreira, TAE ;
Acioli, LH ;
Machado, FLA .
SOLID STATE COMMUNICATIONS, 2001, 118 (01) :37-41
[6]   Synthesis of nano-RuAl by mechanical alloying [J].
Liu, KW ;
Mücklich, F ;
Birringer, R .
INTERMETALLICS, 2001, 9 (01) :81-88
[7]  
LIU KW, 1989, J MATER RES, V4, P292
[8]  
MACHADO FLA, 1987, SOLID STATE COMMUN, V61, P45
[9]   A study of the Al-rich part of the Al-Ru alloy system [J].
Mi, S ;
Balanetskyy, S ;
Grushko, B .
INTERMETALLICS, 2003, 11 (07) :643-649
[10]  
Schechtmann D., 1984, PHYS REV LETT, V53, P1951
1