Corrosion performance of waterborne epoxy coatings containing polyethylenimine treated mesoporous-TiO2 nanoparticles on mild steel

被引：82
作者：
Wang, Na [1 ]
Fu, Wanlu [1 ]
Zhang, Jing [1 ]
Li, Xuri [1 ]
Fang, Qinghong [1 ]
机构：
[1] Shenyang Univ Chem Technol, Coll Mat Sci & Engn, Shenyang 110142, Peoples R China
来源：
PROGRESS IN ORGANIC COATINGS | 2015年 / 89卷
基金：
中国国家自然科学基金;
关键词：
Polyethylenimine (PEI); Mesoporous-TiO2 (meso-TiO2); Waterborne epoxy; EIS; NANO-ZNO PARTICLES; TIO2; NANOPARTICLES; IMPROVEMENT; PROTECTION; RESISTANCE; AA2024-T3; PIGMENT; POWDER; MCM-41; AGENT;
D O I：
10.1016/j.porgcoat.2015.07.009
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Waterborne epoxy coatings were modified by adding mesoporous-TiO2 nanoparticles (meso-TiO2). In order to achieve proper dispersion of meso-TiO2 in the epoxy-based coating and make possible chemical interactions between meso-TiO2 and polymeric coating, meso-TiO2 was treated with polyethylenimine (PEI) of various molecular weights. Corrosion performance of mild steel coated specimens was investigated employing electrochemical impedance spectroscopy (EIS) and salt spray test. Coatings with meso-TiO2/PEI (600 molecular weight) possessed the best corrosion performance among the coating specimens. The EIS results showed that the resistance value of coating with meso-TiO2/PEI (600 molecular weight) was above 9.87 x 10(7) Omega cm(2) which was higher than neat epoxy coating. Possible chemical interactions between polymeric matrix and treated nanoparticles caused high barrier properties and high degree of cross-linking. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码：114 / 122
页数：9
相关论文
共 30 条
[11]   Electron Microscopic Study on Aerosol-Assisted Synthesis of Aluminum Organophosphonates Using Flexible Colloidal PS-b-PEO Templates [J].
Kimura, Tatsuo ;
Yamauchi, Yusuke .
LANGMUIR, 2012, 28 (35) :12901-12908
[12]   Silicone functionalized pigment to enhance coating performance [J].
Kumar, K. Rajesh ;
Ghosh, Swapan K. ;
Khanna, A. S. ;
Waghoo, Gulzar ;
Ansari, Faisal ;
Yadav, Kapil .
DYES AND PIGMENTS, 2012, 95 (03) :706-712
[13]   Preparation and characterization of high-refractive-index polymer/inorganic hybrid films containing TiO2 nanoparticles prepared by 4-aminobenzoic acid [J].
Liu, Bo-Tau ;
Li, Pei-Shan .
SURFACE & COATINGS TECHNOLOGY, 2013, 231 :301-306
[14]   Superior gas-sensing and lithium-storage performance SnO2 nanocrystals synthesized by hydrothermal method [J].
Ma, Jianmin ;
Zhang, Jun ;
Wang, Shurong ;
Wang, Qinghong ;
Jiao, Lifang ;
Yang, Jiaqin ;
Duan, Xiaochuan ;
Liu, Zhifang ;
Lian, Jiabiao ;
Zheng, Wenjun .
CRYSTENGCOMM, 2011, 13 (20) :6077-6081
[15]   Effect of curing characterization on the corrosion performance of polyester and polyester/epoxy powder coatings [J].
Mafi, R. ;
Mirabedini, S. M. ;
Naderi, R. ;
Attar, M. M. .
CORROSION SCIENCE, 2008, 50 (12) :3280-3286
[16]   Efficient preparation of hybrid nanocomposite coatings based on poly(vinyl alcohol) and silane coupling agent modified TiO2 nanoparticles [J].
Mallakpour, Shadpour ;
Barati, Abdolvahid .
PROGRESS IN ORGANIC COATINGS, 2011, 71 (04) :391-398
[17]   Multilayer organic-inorganic coating incorporating TiO2 nanocontainers loaded with inhibitors for corrosion protection of AA2024-T3 [J].
Mekeridis, Evaggelos D. ;
Kartsonakis, Ioannis A. ;
Kordas, George .
PROGRESS IN ORGANIC COATINGS, 2012, 73 (2-3) :142-148
[18]   Comparison between the effect of nanoglass flake and montmorillonite organoclay on corrosion performance of epoxy coating [J].
Nematollahi, M. ;
Heidarian, M. ;
Peikari, M. ;
Kassiriha, S. M. ;
Arianpouya, N. ;
Esmaeilpour, M. .
CORROSION SCIENCE, 2010, 52 (05) :1809-1817
[19]   The adhesion properties and corrosion performance of differently pretreated epoxy coatings on an aluminium alloy [J].
Niknahad, M. ;
Moradian, S. ;
Mirabedini, S. M. .
CORROSION SCIENCE, 2010, 52 (06) :1948-1957
[20]   PEI-grafted magnetic porous powder for highly effective adsorption of heavy metal ions [J].
Pang, Ya ;
Zeng, Guangming ;
Tang, Lin ;
Zhang, Yi ;
Liu, Yuanyuan ;
Lei, Xiaoxia ;
Li, Zhen ;
Zhang, Jiachao ;
Xie, Gengxin .
DESALINATION, 2011, 281 :278-284
123