Corrosion performance of waterborne epoxy coatings containing polyethylenimine treated mesoporous-TiO2 nanoparticles on mild steel

被引：82
作者：
Wang, Na [1 ]
Fu, Wanlu [1 ]
Zhang, Jing [1 ]
Li, Xuri [1 ]
Fang, Qinghong [1 ]
机构：
[1] Shenyang Univ Chem Technol, Coll Mat Sci & Engn, Shenyang 110142, Peoples R China
来源：
PROGRESS IN ORGANIC COATINGS | 2015年 / 89卷
基金：
中国国家自然科学基金;
关键词：
Polyethylenimine (PEI); Mesoporous-TiO2 (meso-TiO2); Waterborne epoxy; EIS; NANO-ZNO PARTICLES; TIO2; NANOPARTICLES; IMPROVEMENT; PROTECTION; RESISTANCE; AA2024-T3; PIGMENT; POWDER; MCM-41; AGENT;
D O I：
10.1016/j.porgcoat.2015.07.009
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Waterborne epoxy coatings were modified by adding mesoporous-TiO2 nanoparticles (meso-TiO2). In order to achieve proper dispersion of meso-TiO2 in the epoxy-based coating and make possible chemical interactions between meso-TiO2 and polymeric coating, meso-TiO2 was treated with polyethylenimine (PEI) of various molecular weights. Corrosion performance of mild steel coated specimens was investigated employing electrochemical impedance spectroscopy (EIS) and salt spray test. Coatings with meso-TiO2/PEI (600 molecular weight) possessed the best corrosion performance among the coating specimens. The EIS results showed that the resistance value of coating with meso-TiO2/PEI (600 molecular weight) was above 9.87 x 10(7) Omega cm(2) which was higher than neat epoxy coating. Possible chemical interactions between polymeric matrix and treated nanoparticles caused high barrier properties and high degree of cross-linking. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码：114 / 122
页数：9
相关论文
共 30 条
[1]   The effect of SiO2 filler content and its organic compatibility on thermal stability of epoxy resin [J].
Afzal, Adeel ;
Siddiqi, Humaira M. ;
Iqbal, Naseer ;
Ahmad, Zahoor .
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2013, 111 (01) :247-252
[2]   Corrosion performance of epoxy coatings containing silane treated ZrO2 nanoparticles on mild steel in 3.5% NaCl solution [J].
Behzadnasab, M. ;
Mirabedini, S. M. ;
Kabiri, K. ;
Jamali, S. .
CORROSION SCIENCE, 2011, 53 (01) :89-98
[3]   Synthesis and characterization of zirconium-doped mesoporous nano-crystalline TiO2 [J].
Bineesh, Kanattukara Vijayan ;
Kim, Dong-Kyu ;
Park, Dae-Won .
NANOSCALE, 2010, 2 (07) :1222-1228
[4]   Hierarchical macro/mesoporous TiO2/SiO2 and TiO2/ZrO2 nanocomposites for environmental photocatalysis [J].
Chen, Xiufang ;
Wang, Xinchen ;
Fu, Xianzhi .
ENERGY & ENVIRONMENTAL SCIENCE, 2009, 2 (08) :872-877
[5]   Assessment of organic coating degradation via local impedance imaging [J].
Darowicki, K. ;
Szocinski, M. ;
Zielinski, A. .
ELECTROCHIMICA ACTA, 2010, 55 (11) :3741-3748
[6]   Effect of nano-ZnO particles on the corrosion behavior of alkyd-based waterborne coatings [J].
Dhoke, Shailesh K. ;
Khanna, A. S. ;
Sinha, T. Jai Mangal .
PROGRESS IN ORGANIC COATINGS, 2009, 64 (04) :371-382
[7]   Recent developments in the utilization of green solvents in polymer chemistry [J].
Erdmenger, Tina ;
Guerrero-Sanchez, Carlos ;
Vitz, Juergen ;
Hoogenboom, Richard ;
Schubert, Ulrich S. .
CHEMICAL SOCIETY REVIEWS, 2010, 39 (08) :3317-3333
[8]   Improvement of microalgae harvesting by magnetic nanocomposites coated with polyethylenimine [J].
Hu, Yi-Ru ;
Guo, Chen ;
Wang, Feng ;
Wang, Shi-Kai ;
Pan, Feng ;
Liu, Chun-Zhao .
CHEMICAL ENGINEERING JOURNAL, 2014, 242 :341-347
[9]   Evaluation of the corrosion resistance of anodized aluminum 6061 using electrochemical impedance spectroscopy (EIS) [J].
Huang, Yuelong ;
Shih, Hong ;
Huang, Huochuan ;
Wu, Shun ;
Ramanathan, Sivakami ;
Chang, Chris ;
Mansfeld, Florian .
CORROSION SCIENCE, 2008, 50 (12) :3569-3575
[10]   N-doped TiO2 nanoparticle based visible light photocatalyst by modified peroxide sol-gel method [J].
Jagadale, Tushar C. ;
Takale, Shrikant P. ;
Sonawane, Ravindra S. ;
Joshi, Hrushikesh M. ;
Patil, Shankar I. ;
Kale, Bharat B. ;
Ogale, Satishchandra B. .
JOURNAL OF PHYSICAL CHEMISTRY C, 2008, 112 (37) :14595-14602
123