Effects of Pretreatments on the Adhesion of Acetoacetate to AA2024-T3 Using the Blister Test

被引：2
作者：
Rincon Troconis, Brendy C. [1 ]
Frankel, G. S. [1 ]
机构：
[1] Ohio State Univ, Dept Mat Sci & Engn, Fontana Corros Ctr, Columbus, OH 43210 USA
来源：
CORROSION | 2014年 / 70卷 / 05期
关键词：
AA2024-T3; acetoacetate; adhesion; blister test; conversion coating; cleaning; surface preparation; x-ray photoelectron spectroscopy; CHROMIUM PROCESS COATINGS; ALUMINUM-ALLOYS; CORROSION PROTECTION; CONVERSION COATINGS; ORGANIC COATINGS; COPPER; STRENGTH; FILMS;
D O I：
10.5006/1178
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The blister test was used to assess the effect of various pretreatments, including chromate conversion coatings, non-chromium process conversion coatings, and trivalent chromium process coatings, on the adhesion strength of acetoacetate coatings to aluminum alloy (AA) 2024-T3 (UNS A92024). The effects of cleaning and desmutting prior to conversion coating and improper water rinse temperature after cleaning were also addressed. The results revealed that when properly applied, pretreatments improved the adhesion strength of acetoacetate primer on AA2024-T3. In addition, cleaning and desmutting improved adhesion for all conversion coatings, except for chromate conversion coatings, and the level of adhesion depends on the particular conversion coating used. Process control was found to be of great significance for the performance of acetoacetate coating systems applied on AA2024-T3, as a low rinse water temperature after cleaning resulted in coating blistering.
引用
收藏
页码：483 / 495
页数：13
相关论文
共 52 条
  • [1] THE SOLUBILITY OF AMORPHOUS SILICA IN WATER
    ALEXANDER, GB
    HESTON, WM
    ILER, RK
    [J]. JOURNAL OF PHYSICAL CHEMISTRY, 1954, 58 (06) : 453 - 455
  • [2] [Anonymous], [No title captured]
  • [3] [Anonymous], 1994, B117 ASTM
  • [4] [Anonymous], 1979, CHEM SILICA SOLUBILI
  • [5] [Anonymous], 1997, MILSTD7179 US DEP DE
  • [6] A comparative study of three adhesion tests (EN 5829 similar to ASTM C633, LASAT (LASer Adhesion Test), and bulge and blister test) performed on plasma sprayed copper deposited on aluminium 2017 substrates
    Arrigoni, M.
    Barradas, S.
    Braccini, A.
    Dupeux, M.
    Jeandin, M.
    Boustie, M.
    Bolis, C.
    Berthe, L.
    [J]. JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2006, 20 (05) : 471 - 487
  • [7] Bowles C.A., 1999, TRISERVICE CORR C P
  • [8] THE APPLICATION OF THE BLISTER TEST TO AN ELASTOMERIC ADHESIVE
    BRISCOE, BJ
    PANESAR, SS
    [J]. PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 1991, 433 (1887): : 23 - 43
  • [9] THIN-FILM ADHESION
    CHAPMAN, BN
    [J]. JOURNAL OF VACUUM SCIENCE & TECHNOLOGY, 1974, 11 (01): : 106 - 113
  • [10] Cormier G.J., 1994, ASM Handbook, V5, P18
123456