High-Temperature Oxidation Behavior of a Single-Layer IrAl Intermetallic Coating

被引：2
|
作者：
Zhu, Li'an [1 ]
Ye, Yicong [1 ]
Bai, Shuxin [1 ]
Zhang, Hong [1 ]
Zhang, Kaili [1 ]
Ai, Yuanlin [1 ]
Li, Shun [1 ]
Tang, Yu [1 ]
机构：
[1] Natl Univ Def Technol, Coll Aerosp Sci & Engn, Dept Mat Sci & Engn, Changsha 410073, Hunan, Peoples R China
来源：
OXIDATION OF METALS | 2019年 / 91卷 / 5-6期
基金：
中国国家自然科学基金;
关键词：
Iridium aluminide; Pack cementation; Intermetallics; Cyclic oxidation; IRIDIUM-ALUMINUM;
D O I：
10.1007/s11085-019-09907-z
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
In order to improve the high-temperature service property of Ir, a well-bonded single-layer pure IrAl intermetallic coating was prepared on Ir by pack cementation followed by vacuum annealing treatment. The oxidation behavior of the IrAl coating was investigated by cyclic oxidation tests at 1400-2000 degrees C and compared with that of pure Ir. The results showed that the IrAl coating, although containing many cracks, exhibited excellent oxidation resistance over the whole experimental temperature range. The reasons were deduced to be the in situ formation of Al2O3 and the sintering of the cracks in the IrAl layer. The excellent oxidation protective effect of the single-layer IrAl coating can be ascribed to its stable and unique as-oxidized microstructure, i.e., double-layer structure of Al2O3/Ir, which showed excellent compatibility and comprehensive property.
引用
收藏
页码：749 / 766
页数：18
相关论文
共 50 条
  • [11] High-temperature mechanical properties of B2 type IrAl intermetallic compounds doped with Ni
    Ono, T
    Chiba, A
    Li, XG
    Takahashi, S
    MATERIALS TRANSACTIONS JIM, 1997, 38 (02): : 171 - 174
  • [12] High-temperature oxidation behavior and surface roughness evolution of VPSNiCrAlY coating
    Seo, D.
    Ogawa, K.
    Shoji, T.
    Murata, S.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2008, 17 (01) : 136 - 143
  • [13] High-temperature mechanical behavior of B2 type IrAl doped with Ni
    Chiba, A
    Ono, T
    Li, XG
    Takahashi, S
    HIGH-TEMPERATURE ORDERED INTERMETALLIC ALLOYS VII, 1997, 460 : 707 - 712
  • [14] Distinctive Characteristics of Multilayer and Single-Layer Coatings under High-Temperature Testing
    Vorontsov, A. V.
    Filippov, A. V.
    Shamarin, N. N.
    Moskvichev, E. N.
    Novitskaya, O. S.
    Knyazhev, E. O.
    Denisova, Yu. A.
    Leonov, A. A.
    Denisov, V. V.
    JOURNAL OF SURFACE INVESTIGATION, 2023, 17 (SUPPL 1): : S96 - S103
  • [15] Distinctive Characteristics of Multilayer and Single-Layer Coatings under High-Temperature Testing
    A. V. Vorontsov
    A. V. Filippov
    N. N. Shamarin
    E. N. Moskvichev
    O. S. Novitskaya
    E. O. Knyazhev
    Yu. A. Denisova
    A. A. Leonov
    V. V. Denisov
    Journal of Surface Investigation: X-ray, Synchrotron and Neutron Techniques, 2023, 17 : S96 - S103
  • [16] High-temperature Oxidation Behavior and Surface Roughness Evolution of VPS NiCrAlY Coating
    D. Seo
    K. Ogawa
    T. Shoji
    S. Murata
    Journal of Thermal Spray Technology, 2008, 17 : 136 - 143
  • [17] Effect of Sputtered AlY Coating on High-Temperature Oxidation Behavior of Stainless Steel
    Fu, Guangyan
    Xie, Huanzhang
    Su, Yong
    Qi, Zeyan
    Hou, Qiang
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2016, 35 (07) : 677 - 683
  • [18] Improvement of the tribological and high-temperature oxidation behavior of mild steel by alumina coating
    Bhargav, Amit
    Sasikumar, C.
    Lodhe, Mangesh
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2024,
  • [19] Influence of Re on High-Temperature Oxidation Behavior of MCrAIY Type Coating Alloys
    Shahzad Salem
    Zhang Yuduo
    Wang Haifeng
    Yang Zhigang
    Zhang Chi
    RARE METAL MATERIALS AND ENGINEERING, 2015, 44 : 316 - 319
  • [20] High temperature oxidation behavior of NiTiNb intermetallic alloys
    Zhao, Xinqing
    Xu, Jian
    Tang, Liang
    Gong, Shengkai
    INTERMETALLICS, 2007, 15 (08) : 1105 - 1115
12345