Fire-safe agent integrated with oyster shell and melamine polyphosphate for thermoplastic polyurethane

At present, thermoplastic polyurethane (TPU) is widely used, but there are still many defects in fire safety, such as burning with heavy smoke and dripping. In this article, OS@MP was synthesized by modifying oyster shell (OS) powder with melamine polyphosphate (MP) and then served as fire-safe agent for TPU. The fire performance of TPU composites were investigated using microscale combustion colorimeter (MCC), cone calorimeter test (CCT), smoke density test (SDT), and thermogravimetric analysis/Fourier transform infrared (TG-FTIR) spectrum analysis. The MCC and CCT results revealed that OS@MP could reduce the fire hazards of TPU composites. The peak heat release rate (pHRR) of the sample with 10.0 wt% OS@MP decreased to 170.86 kW/m(2) from 1772.37 kW/m(2) for pure TPU. And, the SDT results showed that OS@MP could significantly reduce the smoke production of TPU composites. The TG-FTIR also confirmed that the noncombustible gases (including CO2, ammonia, and water vapor) produced by OS@MP have played a reinforcing role in TPU composites as well as a char formed on the surface of composites, which could act as a barrier to prevent the heat and air, reinforce the fire safety of TPU.