Glass-ceramic glazes in the CaO-SiO2 system

被引：6

作者：

Alptekin, K ^{[1
]}

Kara, F ^{[1
]}

机构：

[1] Anadolu Univ, Dept Mat Sci & Engn, TR-26555 Eskisehir, Turkey

来源：

EURO CERAMICS VIII, PTS 1-3 | 2004年 / 264-268卷

关键词：

glass-ceramic glaze; crystalline glaze; wollastonite glaze;

D O I：

10.4028/www.scientific.net/KEM.264-268.1709

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Glass ceramic glazes were developed in the system of CaO-SiO2 system. Compositions containing B2O3 and K2O as fluxing agent were melted at 1450degreesC and fritted. Glazes for porcelain tiles were formulated by using these frits. It was observed that wollastonite crystals were formed under industrial fast firing conditions with a peak temperature over 1200degreesC. Chemical and wear behaviours of the wollastonite containing glazes and the morphology of the crystals were examined.

引用

页码：1709 / 1712

页数：4

共 7 条

[1] Thermal and chemical properties of diopside-wollastonite glass-ceramics in the SiO2-CaO-MgO system from raw materials [J].

Abdel-Hameed, SAM ;

El-Kheshen, AA .

CERAMICS INTERNATIONAL, 2003, 29 (03) :265-269

[2] Effect of devitrification on frit particle sintering during firing [J].

Amorós, JL ;

Escardino, A ;

Gozalbo, A ;

Orts, MJ .

EURO CERAMICS VII, PT 1-3, 2002, 206-2 :2053-2056

[3] EFFECTS OF NUCLEATING-AGENTS ON DIOPSIDE CRYSTALLIZATION IN NEW GLASS-CERAMICS FOR TILE-GLAZE APPLICATION [J].

BALDI, G ;

GENERALI, E ;

LEONELLI, C ;

MANFREDINI, T ;

PELLACANI, GC ;

SILIGARDI, C .

JOURNAL OF MATERIALS SCIENCE, 1995, 30 (12) :3251-3255

[4] Feasibility of using cordierite class-ceramics as tile glazes [J].

Ferrari, AM ;

Barbieri, L ;

Leonelli, C ;

Manfredini, T ;

Siligardi, C ;

Corradi, AB .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1997, 80 (07) :1757-1766

[5]

PREDA M, 1997, KEY ENG MATER, V132, P214

[6]

QUINTEIRO E, 2002, QUALICER, P301

[7] Effect of iron oxide content on the crystallisation of a diopside glass-ceramic glaze [J].

Romero, M ;

Rincón, JM ;

Acosta, A .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (06) :883-890

← 1 →