Modification of a carbon/carbon composite with a thermosetting resin precursor as a matrix by the addition of carbon black

Carbon/carbon composites were made through the pyrolysis of stabilized PAN felt and phenolic resin with the addition of 5 or 10 wt % carbon black to the matrix and then heat treatment at 600-2500 degrees C. The effects of adding carbon black to the matrix precursor on the physical properties, microstructure, and mechanical properties of the resultant composites were investigated. Adding carbon black not only reduced the weight loss but also limited the shrinkage of the resultant composites. Adding carbon black also accelerated the formation of carbon basal planes in the matrix. At 2500 degrees C, the crystalline stacking height in the composite with 10 wt % added carbon black was 200% greater than that with no additive. The flexural strength of the composite also increased from 15 to 42 MPa (almost 300%). (c) 2006 Wiley Periodicals, Inc.