Influence of Extrusion Temperature on Microstructure of Ti-47A1-2Cr-2Nb-0. 15B

被引：0

作者：

Liu, Renci ^{[1
]}

Liu, Dong ^{[1
]}

Cui, Yuyou ^{[1
]}

Yang, Rui ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China

来源：

TI-2011: PROCEEDINGS OF THE 12TH WORLD CONFERENCE ON TITANIUM, VOL II | 2012年

关键词：

gamma-titanium aluminide (TiAI); extrusion temperature; microstructure; thermomechanical treatment; GAMMA-TITANIUM ALUMINIDE; ALLOYS;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Influences of extrusion temperature on the deformed and subsequently thermomechanically treated lamellar (TMTL) microstructures of Ti47A1-2Cr-2Nb-0. 15B alloy as observed on the transverse section were investigated. Canned ingots were axisymmetrically-extruded through a flat die to an extrusion ratio of 8 1. The extruded rods on the transverse section consisted of fine duplex microstructure at the edge and fully lamellar (FL) at the center. However, the FL microstructure at the center changed with increasing extrusion temperature: the rods contained remnant lamellae and partially recrystallized FL grains after extrusion at 1250 degrees C and 1280 degrees C, and consisted of completely recrystallized grains after extrusion at 1300 degrees C, with the size and volume fraction of the recrystallized FL grains increasing with the increase of extrusion temperature. The heterogeneity of deformed and TMTL microstructures is believed to be caused by nonuniform deformation and temperature distribution due to deformation heating and die chilling.

引用

页码：1553 / 1557

页数：5

共 15 条

[1]

Appel F, 2000, ADV ENG MATER, V2, P699, DOI 10.1002/1527-2648(200011)2:11<699::AID-ADEM699>3.0.CO

[2]

2-J

[3]

Austin CM, 1997, STRUCTURAL INTERMETA, P413

[4] Three-dimensional finite element modelling of a titanium aluminide aerofoil forging [J].

Brooks, JW ;

Dean, TA ;

Hu, ZM ;

Wey, E .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1998, 80-1 :149-155

[5] Microstructure development in gamma alloy mill products by thermomechanical processing [J].

Dimiduk, DM ;

Martin, PL ;

Kim, YW .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 243 (1-2) :66-76

[6] Supertransus processing of TiAl-based alloys [J].

Fuchs, GE .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (01) :27-36

[7] EFFECT OF CORE INSULATION ON THE QUALITY OF THE EXTRUDATE IN CANNED EXTRUSIONS OF GAMMA-TITANIUM ALUMINIDE [J].

GOETZ, RL ;

JAIN, VK ;

LOMBARD, CM .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1992, 35 (01) :37-60

[8] The adiabatic correction factor for deformation heating during the uniaxial compression test [J].

Goetz, RL ;

Semiatin, SL .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2001, 10 (06) :710-717

[9]

Huang S.C., 1995, INTERMETALLIC COMPOU, V2, P73

[10]

Kim YW, 1995, GAMMA TITANIUM ALUMINIDES, P637

← 1 2 →