Oxidation behavior of multiphase Mo-Si-B alloys

被引：44
|
作者：
Supatarawanich, V [1 ]
Johnson, DR
Liu, CT
机构：
[1] Purdue Univ, Sch Mat Engn, W Lafayette, IN 47907 USA
[2] Oak Ridge Natl Lab, Div Met & Ceram, Oak Ridge, TN 37831 USA
来源：
INTERMETALLICS | 2004年 / 12卷 / 7-9期
关键词：
multiphase intermetallics; silicides; various; oxidation;
D O I：
10.1016/j.intermet.2004.02.011
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The oxidation behavior of multiphase Mo, Mo3Si, and Mo5SiB2 (T2) alloys was examined at 800 and 1300 degreesC. The alloys were cast and heat treated at 1600 degreesC before the cyclic oxidation tests were performed. The compositions of the alloys with SUB ratios of 0.5, 0.71, and 1.0 were chosen near the L = (Mo) + T2 eutectic trough to produce a fine dispersion of the different phases. The multiphase alloys showed poor oxidation resistance at 800 degreesC while a protective glass scale formed at 1300 degreesC. At 800 degreesC the oxidation resistance improved as the volume fraction of the T2 phase increased. Conversely, at 1300 degreesC, the glass scaled that formed on the alloys with a SUB ratio of 0.5 was not protective. However, a protective glass scale did form on the alloys with a higher SUB ratio. The near eutectic alloy with a SUB = 1 was found to have the best oxidation resistance at 1300 degreesC. The results indicate the Mo3Si phase provides a source of silicon for controlling the composition of the glass scale at 1300 degreesC. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：721 / 725
页数：5
相关论文
共 50 条
  • [21] Growth Kinetics and Isothermal Oxidation Behavior of Aluminide Pack Coatings on a Multiphase Mo-Si-B Alloy
    Choi, Kwangsu
    Yang, Wonchul
    Baik, Kyeong-Ho
    Kim, Youngmoo
    Lee, Seong
    Park, Joon Sik
    OXIDATION OF METALS, 2019, 92 (5-6): : 423 - 437
  • [22] Oxidation behavior of Mo-Si-B in-situ composites
    Yamauchi, Akira
    Yoshimi, Kyosuke
    Murakami, Yoshihiro
    Kurokawa, Kazuya
    Hanada, Shuji
    DESIGNING OF INTERFACIAL STRUCTURES IN ADVANCED MATERIALS AND THEIR JOINTS, 2007, 127 : 215 - +
  • [23] Microstructure and oxidation behavior of Mo-Si-B ternary silicide
    Wang Fang
    Shan Meng
    Shan Aidang
    Wu Jiansheng
    RARE METAL MATERIALS AND ENGINEERING, 2006, 35 (12) : 1920 - 1923
  • [24] Oxidation of Mo-Si-B Alloys and Coatings in a Water Vapor Environment
    Perepezko, J. H.
    Harris, C.
    OXIDATION OF METALS, 2021, 96 (3-4): : 323 - 332
  • [25] Polymer derived oxidation barrier coatings for Mo-Si-B alloys
    Smokovych, Iryna
    Hasemann, Georg
    Krueger, Manja
    Scheffler, Michael
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2017, 37 (15) : 4559 - 4565
  • [26] Oxidation of Mo-Si-B Alloys and Coatings in a Water Vapor Environment
    J. H. Perepezko
    C. Harris
    Oxidation of Metals, 2021, 96 : 323 - 332
  • [27] Oxidation Performance of High Temperature Mo-Si-B Alloys and Coatings
    Perepezkoa, J. H.
    Rioult, F.
    Sakidja, R.
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 7, PTS 1 AND 2, 2008, 595-598 : 1065 - 1074
  • [28] Deformation behavior of a multiphase fine-grained Mo-Si-B alloy
    Yu, J. L.
    Li, Z. K.
    Zheng, X.
    Li, H.
    Wang, D. H.
    Zhang, J. J.
    Wang, H.
    MATERIALS AND DESIGN, PTS 1-3, 2011, 284-286 : 544 - 549
  • [29] Oxidation behavior of pack-cemented Si-B oxidation protection coatings for Mo-Si-B alloys at 1300 °C
    Lange, Annika
    Heilmaier, Martin
    Sossamann, Travis A.
    Perepezko, John H.
    SURFACE & COATINGS TECHNOLOGY, 2015, 266 : 57 - 63
  • [30] High temperature oxidation of mechanically alloyed Mo-Si-B alloys
    Burk, S.
    Gorr, B.
    Trindade, V. B.
    Krupp, U.
    Christ, H. -J.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2009, 44 (03) : 168 - 175
12345