Microstructure and high-temperature oxidation resistance of MoSi2-ZrO2 composite coatings for Niobium substrate

被引：41

作者：

Zhu, Lu ^{[1
,2
]}

Ren, Xuanru ^{[1
]}

Wang, Xiaohong ^{[1
]}

Kang, Xueqin ^{[1
]}

Zheng, Ruixin ^{[1
]}

Feng, Peizhong ^{[1
]}

机构：

[1] China Univ Min & Technol, Sch Mat Sci & Engn, Xuzhou 221116, Jiangsu, Peoples R China

[2] China Univ Min & Technol, Sch Chem Engn & Technol, Xuzhou 221116, Jiangsu, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2021年 / 41卷 / 02期

基金：

中国国家自然科学基金;

关键词：

spent MoSi2; ZrO2; oxidation behavior; Niobium substrate; spark plasma sintering; MECHANICAL-PROPERTIES; C/C COMPOSITES; MOSI2-BASED COMPOSITE; THERMAL-EXPANSION; SPRAYED MOSI2; BEHAVIOR; ALLOY; PROTECTION; EVOLUTION; PHASE;

D O I：

10.1016/j.jeurceramsoc.2020.09.029

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Spent MoSi2 heating elements, which worked in the industrial electrical furnace at high temperature, were crushed into powders and reused as coating raw materials. ZrO2 was added into spent MoSi2 powders to fabricate MoSi2-ZrO2 coatings on niobium by spark plasma sintering, and the microstructure and oxidation behavior of the coatings at 1500 and 1700 degrees C were explored. The results showed that cracks exist in MoSi2 coating while ZrO2 containing coatings are crack-free with the formation of (Mo,Nb)(5)Si-3 diffusion layer after SPS, indicating good metallurgical bonding. After oxidation at 1500 degrees C for 20 h, the lowest mass gain is obtained by MoSi2-30ZrO(2) coating. SiO2 and ZrSiO4 are formed on the composite coatings at elevated temperature, which improves the high-temperature oxidation resistance. After oxidation at 1700 degrees C for 60 min, the oxide scale of MoSi2-30ZrO(2) coating is dense without any voids or cracks, demonstrating better high-temperature oxidation resistance than that of single MoSi2 coating.

引用

页码：1197 / 1210

页数：14

共 81 条

[1] Oxidation kinetics of Zircaloy-4 and Zr-1Nb-1Sn-0.1Fe at temperatures of 700-1200°C [J].

Baek, JH ;

Park, KB ;

Jeong, YH .

JOURNAL OF NUCLEAR MATERIALS, 2004, 335 (03) :443-456

[2]

Bansal N.P., 2005, HDB CERAMIC COMPOSIT

[3] SiC/MoSi2 based coatings for Cf/C composites by two step pack cementation [J].

Bezzi, Federica ;

Burgio, Federica ;

Fabbri, Paride ;

Grilli, Selene ;

Magnani, Giuseppe ;

Salernitano, Elena ;

Scafe, Matteo .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2019, 39 (01) :79-84

[4]

BIZZARRI V, 1989, AM CERAM SOC BULL, V68, P1834

[5] Oxidation of niobium sheets at high temperature [J].

Bouillet, C ;

Ciosmak, D ;

Lallemant, M ;

Laruelle, C ;

Heizmann, JJ .

SOLID STATE IONICS, 1997, 101 :819-824

[6]

Cai Z., 2002, DICT CERAMIC MAT

[7] Development of Protective Coating of MoSi2 over TZM Alloy Substrate by Slurry Coating Technique [J].

Chakraborty, S. P. .

MATERIALS TODAY-PROCEEDINGS, 2016, 3 (09) :3071-3076

[8] Development of silicide coating over molybdenum based refractory alloy and its characterization [J].

Chakraborty, S. P. ;

Banerjee, S. ;

Sharma, I. G. ;

Suri, A. K. .

JOURNAL OF NUCLEAR MATERIALS, 2010, 403 (1-3) :152-159

[9] Effect of scandia content on the hot corrosion behavior of Sc2O3 and Y2O3 co-doped ZrO2 in Na2SO4 + V2O5 molten salts at 1000 °C [J].

Chen, Chao ;

Liang, Tianquan ;

Guo, Yan ;

Chen, Xiyong ;

Man, Quanyan ;

Zhang, Xiuhai ;

Zeng, Jianmin ;

Ji, Vincent .

CORROSION SCIENCE, 2019, 158

[10] Preparation of oxidation protective MoSi2-SiC coating on graphite using recycled waste MoSi2 by one-step spark plasma sintering method [J].

Chen, Peng ;

Zhu, Lu ;

Ren, Xuanru ;

Kang, Xueqin ;

Wang, Xiaohong ;

Feng, Peizhong .

CERAMICS INTERNATIONAL, 2019, 45 (17) :22040-22046

← 1 2 3 4 5 6 7 8 9 →