Experimental study on 830 Mpa grade pipeline steel containing chromium

被引：8

作者：

Ren, Yi ^{[1
]}

Zhang, Shuai ^{[1
]}

Wang, Shuang ^{[1
]}

Liu, Wen-yue ^{[1
]}

机构：

[1] Anshan Iron & Steel Co Ltd, Ctr Tech, Anshan 114009, Peoples R China

来源：

INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS | 2009年 / 16卷 / 03期

关键词：

chromium; high strength; pipeline steel; thermo-mechanical controlled process; MECHANICAL-PROPERTIES;

D O I：

10.1016/S1674-4799(09)60049-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The diversity of microstructure and properties of 830 MPa grade pipeline steel containing chromium was investigated by optical microscope and transmission electron microscopy. The main microstructures were multiple configurations, containing lath bainite and granule bainite. Mechanical properties test results showed that the yield strength and tensile strength improved with increasing chromium content. The toughness and elongation decreased at the same time, so temper process was introduced. Appling proper temper parameters, the values of toughness and elongation were improved dramatically, and the strength decreased slightly.

引用

页码：273 / 277

页数：5

共 17 条

[1] A STUDY OF MULTIPLE MICROALLOYED PIPELINE STEELS [J].

EMENIKE, COI .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1990, 9 (04) :406-409

[2]

FAIRCHILD P, 2005, SEM FOR X100 120 GRA, P223

[3]

HUANG KW, 2003, WELD PIPE TUBE, V26, P1

[4]

Li H. L., 2004, WELDED PIPE TUBE, V27, P1

[5]

Okaguchi S, 2003, INT OFFSHORE POLAR E, P36

[6]

[任毅 REN Yi], 2007, [北京科技大学学报, Journal of University Science and Technology Beijing], V29, P798

[7] Microstructure of high strength niobium-containing pipeline steel [J].

Shanmugam, S. ;

Misra, R. D. K. ;

Hartmann, J. ;

Jansto, S. G. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 441 (1-2) :215-229

[8] Transmission electron microscopy of martensite/austenite islands in pipeline steel X70 [J].

Wang, Chunming ;

Wu, Xingfang ;

Liu, Jie ;

Xu, Ning'an .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 438 (267-271) :267-271

[9]

[王春明 WANG Chunming], 2006, [北京科技大学学报, Journal of University Science and Technology Beijing], V28, P253

[10]

Wang Yong, 2005, X100 X120 HIGH STREN, P6

← 1 2 →