Hot-dip Galvanizing of Carbon Steel after Cold Rolling with Oxide Scale and Hydrogen Descaling

被引：17

作者：

He, Yong-quan ^{[1
]}

Jia, Tao ^{[1
]}

Liu, Xiao-jiang ^{[1
]}

Cao, Guang-ming ^{[1
]}

Liu, Zhen-yu ^{[1
]}

Li, Jun ^{[1
,2
]}

机构：

[1] Northeastern Univ, State Key Lab Rolling & Automat, Shenyang 110819, Peoples R China

[2] Baosteel Res Inst, Shanghai 201900, Peoples R China

来源：

JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL | 2014年 / 21卷 / 02期

关键词：

oxide scale; acid-free cleaning; cold rolling; reducing annealing; hot-dip galvanizing; DEFORMATION; REDUCTION; FRACTURE; FAILURE; TENSILE; IRON;

D O I：

10.1016/S1006-706X(14)60034-0

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

A new processing method for producing hot-dip galvanized steel is designed and tested, in which pickling is skipped. Hot-rolled low carbon steel sheets are rolled with oxide scale in an experimental mill at room temperature, prior to annealing under a 20% hydrogen reducing atmosphere and galvanizing on a hot-dip galvanizing simulator. Micro-cracks formed in the oxide scale during cold rolling roughen the steel surface and enlarge the specific surface. Through-thickness cracks provide transport channels for hydrogen, and hence the reduction of oxide scale is enhanced. When the sheet is dipped in the zinc bath, cracks are submerged by liquated zinc and the defects are not distinct after hot-dip galvanizing. The overlay coating occludes with rough surface of the sheet, whereby a superior coating adherence is realized.

引用

页码：222 / 226

页数：5

共 14 条

[1] FRACTURE MECHANISMS IN OXIDE SCALE ON IRON DURING SUBSTRATE DEFORMATION [J].

CHAUDHURI, SK ;

ROLLS, R .

JOURNAL OF MATERIALS SCIENCE, 1977, 12 (11) :2303-2309

[2] Deformation of iron oxides upon tensile tests at 600-1250°C [J].

Hidaka, Y ;

Anraku, T ;

Otsuka, N .

OXIDATION OF METALS, 2003, 59 (1-2) :97-113

[3]

Hudson R., 1985, MET FINISH, V83, P59

[4]

Hudson R.M., 1985, MET FINISH, V83, P73

[5] Analysis of secondary oxide-scale failure at entry into the roll gap [J].

Krzyzanowski, M ;

Beynon, JH ;

Sellars, CM .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2000, 31 (06) :1483-1490

[6] Modelling the behaviour of oxide scale in hot rolling [J].

Krzyzanowski, Michal ;

Beynon, John Howard .

ISIJ INTERNATIONAL, 2006, 46 (11) :1533-1547

[7] Surface oxide fracture in cold aluminium rolling [J].

Le, HR ;

Sutcliffe, MPF ;

Wang, PZ ;

Burstein, GT .

ACTA MATERIALIA, 2004, 52 (04) :911-920

[8] Cracking and deformation of surface scale during hot rolling of steel [J].

Li, YH ;

Sellars, CM .

MATERIALS SCIENCE AND TECHNOLOGY, 2002, 18 (03) :304-311

[9] The metallurgy of zinc-coated steel [J].

Marder, AR .

PROGRESS IN MATERIALS SCIENCE, 2000, 45 (03) :191-271

[10]

Masaaki U., 1995, ISJI INT, V81, P129

← 1 2 →