Low temperature spark plasma sintering of Al2O3-TiC composites

被引：21
|
作者：
Meir, S. [1 ]
Kalabukhov, S. [1 ]
Hayun, S. [1 ]
机构：
[1] Ben Gurion Univ Negev, Dept Mat Engn, IL-84105 Beer Sheva, Israel
来源：
CERAMICS INTERNATIONAL | 2014年 / 40卷 / 08期
关键词：
Aluminum oxide; Ceramic composite; Spark plasma sintering (SPS); Titanium carbide; MECHANICAL-PROPERTIES; MICROSTRUCTURE; TOOLS;
D O I：
10.1016/j.ceramint.2014.04.059
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Al2O3-TiC composites were fabricated using spark plasma sintering (SPS) technology between 1300 degrees C and 1500 degrees C. The composite densification process starts at 950 degrees C, with a maximum densification rate at 1170 degrees C. After thirty minutes soaking at 1400 degrees C, a relative density of 99.5% was achieved. Microstructure analysis reveals a submicron Al2O3 grain size and homogenous distribution of titanium carbide in the matrix. The fully dense Al2O3-20 wt% TiC composite exhibits high values of fracture toughness (8.3 MPa m(1/2)), Young's modulus (406 GPa), flexural strength (850 MPa) and hardness (21 GPa). (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：12187 / 12192
页数：6
相关论文
共 50 条
  • [21] Solid solution formation during spark plasma sintering of ZrB2-TiC-graphite composites
    Istgaldi, Hamid
    Asl, Mehdi Shahedi
    Shahi, Peyman
    Nayebi, Behzad
    Ahmadi, Zohre
    CERAMICS INTERNATIONAL, 2020, 46 (03) : 2923 - 2930
  • [22] Synthesis of Al2O3-TiC by reactive milling
    Pallone, EMJA
    Tomasi, R
    Botta, WJ
    METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, PTS 1 AND 2, 2000, 343-3 : 393 - 398
  • [23] Characteristics of quadruplet Ti-Mo-TiB2-TiC composites prepared by spark plasma sintering
    Nguyen, Thang Phan
    Delbari, Seyed Ali
    Azizian-Kalandaragh, Yashar
    Babapoor, Aziz
    Quyet Van Le
    Namini, Abbas Sabahi
    Shokouhimehr, Mohammadreza
    Asl, Mehdi Shahedi
    CERAMICS INTERNATIONAL, 2020, 46 (13) : 20885 - 20895
  • [24] Spark Plasma Sintering and Characterization of Al-TiB2Composites
    Annamalai, A. Raja
    Srikanth, Muthe
    Muthuchamy, A.
    Acharya, Shashank
    Khisti, Anup
    Agrawal, Dinesh K.
    Jen, Chun-Ping
    METALS, 2020, 10 (09) : 1 - 12
  • [25] Preparation and reparation and mechanical properties of nanocobalt coated Al2O3-TIC composites
    Yin, Yansheng
    Chen, Shougang
    Chang, Xueting
    Lau, Kin-tak
    ADVANCES IN COMPOSITE MATERIALS AND STRUCTURES, PTS 1 AND 2, 2007, 334-335 : 913 - +
  • [26] Spark plasma sintering of TiC particle-reinforced molybdenum composites
    Ohser-Wiedemann, R.
    Weck, Ch.
    Martin, U.
    Mueller, A.
    Seifert, H. J.
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2012, 32 : 1 - 6
  • [27] Synthesis and characterisation of Al2O3/Ni-type composites obtained by spark plasma sintering
    Voicu, Cristina
    Popa, Florin
    Marinca, Traian Florin
    Neamtu, Bogdan Viorel
    Lostun, Mihaela
    Lupu, Nicoleta
    Chicinas, Ionel
    POWDER METALLURGY, 2018, 61 (03) : 251 - 257
  • [28] Densification and microstructure of Al2O3-cBN composites prepared by spark plasma sintering
    Hotta, Mikinori
    Goto, Takashi
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2008, 116 (1354) : 744 - 748
  • [29] Fabrication of Al2O3-Y3Al5O12-ZrO2 composites by single-step spark plasma sintering
    Vakhshouri, Maryam
    Talimian, Ali
    Najafzadehkhoee, Aliasghar
    Gallardo-Lopez, Angela
    Poyato, Rosalia
    Gutierrez-Mora, Felipe
    Galusek, Dusan
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2025, 45 (10)
  • [30] Densification, microstructure, and fracture behavior of TiC/Si3N4 composites by spark plasma sintering
    Bai Ling
    Ge Changchun
    Shen Weiping
    Mao Xiaodong
    Zhang Ke
    RARE METALS, 2008, 27 (03) : 315 - 319
12345