Effects of annealing on nanocrystalline Bi2S3 thin films prepared by chemical bath deposition

Nanocrystalline Bi2S3 thin films are deposited on tin chloride treated glass substrate from the solution containing bismuth nitrate, triethanolamine (TEA) and thioacetamide (TAM) at a bath temperature 318 K. The prepared films are subsequently annealed at different temperatures for studying the effect of thermal treatment on the structural, surface morphology, optical and electrical properties of the films. The X-ray diffraction studies affirmed that the deposited films are orthorhombic structures with average crystallites size of 14 nm to 28 nm. The scanning electron microscopy (SEM) images revealed that the films comprise of grains of spherical shape of unequal size. It is also observed that the small particles aggregate together to form a larger cluster. The average grain sizes determined from the TEM images are smaller than the crystallites size obtained from the XRD studies. The optical band gap of the films has been estimated to be 2.24-2.05 eV for the as-prepared and annealed films, respectively. The electrical conductivity of the as prepared Bi2S3 films at room temperature is found to be in the order of 10(-3) Omega(-1) m(-1). (C) 2014 Elsevier Ltd. All rights reserved.