Improvement of Coercivity and Curie Temperature of Sintered Nd-Fe-B Permanent Magnets by Addition of Cu and Ni

被引：2

作者：

Basoglu, M. ^{[1
]}

Yanmaz, E. ^{[2
]}

机构：

[1] Gumushane Univ, Dept Energy Syst Engn, TR-29100 Gumushane, Turkey

[2] Karadeniz Tech Univ, Dept Phys, TR-61080 Trabzon, Turkey

来源：

JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM | 2014年 / 27卷 / 10期

关键词：

Nd-Fe-B magnets; Sintered magnets; Blending addition; Copper; Nickel; MICROSTRUCTURE; POWDER;

D O I：

10.1007/s10948-014-2582-4

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Sintered Nd-Fe-B magnets are some of the strongest magnetic materials showing magnetic properties. Blending addition is frequently performed in order to improve the magnetic properties of these materials. In this work, high-melting point Ni and low-melting point Cu were added to Nd15Fe77B8 ingot by blending. As a result of structural analysis, it was observed that 0.2 wt% Cu + Ni addition improved the structure of the material; on the other hand, excessive addition resulted in porosity. It was also observed that 0.2 wt% addition improved the magnetic properties, and Curie temperature increased with increasing addition ratio.

引用

页码：2295 / 2298

页数：4

共 6 条

[1] Production of (Nd,MM)2(Fe,Co,Ni)14B-type sintered magnets using a binary powder blending technique [J].

Hosseini, HRM ;

Kianvash, A ;

Reihani, MS ;

Zadeh, HY .

JOURNAL OF ALLOYS AND COMPOUNDS, 2000, 298 (1-2) :319-323

[2] ND - FE - B - CU HD-PROCESSED SINTERED MAGNETS - PROPERTIES AND MICROSTRUCTURE [J].

KNOCH, KG ;

KIANVASH, A ;

HARRIS, IR .

IEEE TRANSACTIONS ON MAGNETICS, 1992, 28 (05) :2142-2144

[3] The effects of blending additions of copper and cobalt to Nd16Fe76B8 milled powder to produce sintered magnets [J].

Mottram, RS ;

Williams, AJ ;

Harris, IR .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2001, 234 (01) :80-89

[4] Improvement of coercivity of sintered NdFeB permanent magnets by heat treatment [J].

Vial, F ;

Joly, F ;

Nevalainen, E ;

Sagawa, M ;

Hiraga, K ;

Park, KT .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2002, 242 :1329-1334

[5] Effects of Mn doping on structural and magnetic properties in NdFeB nanocomposites [J].

Xie, GZ ;

Yin, SL ;

Zhang, FM ;

Lin, PH ;

Gu, BX ;

Lu, M ;

Du, YW ;

Yuan, ZR .

MATERIALS LETTERS, 2004, 58 (05) :636-640

[6] Characterization of microstructure and coercivity of Nd-Fe-B magnets within and Al or Cu addition [J].

Yan, A ;

Song, XP ;

Chen, ZM ;

Wang, XT .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1998, 185 (03) :369-374

← 1 →