Experimental study on CO2 capture mechanisms using Na2ZrO3 sorbents synthesized by soft chemistry method

The CO2 capture performances were demonstrated for Na2ZrO3 sorbents prepared by soft chemistry using varied sodium precursors and drying methods. It was found that Na2C2O4 precursor + heated drying' enabled superior sorption capacity (e.g. 22.77 wt CO2 uptake within 10 min at 800 degrees C in a 15 vol% CO2 stream balanced by N-2) to the other precursor-drying combinations. The as-identified strongest sorbent was further investigated at a series of carbonation temperatures (400-800 degrees C) in N-2-balanced purging streams with 15 vol% and 50 vol% CO2, corresponding post- and pre-combustion CO2 capture scenarios, respectively. The analysis of the resulting sorption capacity, stability and kinetics suggests that sodium diffusion is a more efficient driver than CO2 diffusion for the capture of CO2. Sintering and the subsequent densification inhibits CO2 diffusion but enhances sodium diffusion, which leads to a positive overall effect on the sorption performance. Hence, unlike other high-temperature solid sorbents such as CaO, sintering resistance during cyclic sorption is not a necessity for Na2ZrO3. In addition, higher CO2 fractions in the feed gas improve the sorption kinetics and stability by promoting sodium diffusion as well as CO2 diffusion. (C) 2016 Elsevier B.V. All rights reserved.