Optical properties of ZnNb2O6 single crystals prepared via the optical floating zone technology

被引：9

作者：

Xu, Dapeng ^{[1
]}

Yang, Hang ^{[1
]}

Li, Liang ^{[1
]}

Zhou, Qiang ^{[1
]}

Yuan, Hongming ^{[2
]}

Cui, Tian ^{[1
]}

机构：

[1] Jilin Univ, Coll Phys, State Key Lab Superhard Mat, Changchun 130000, Peoples R China

[2] Jilin Univ, Coll Chem, State Key Lab Inorgan Synth & Preparat Chem, Changchun 130012, Peoples R China

来源：

CRYSTAL RESEARCH AND TECHNOLOGY | 2014年 / 49卷 / 07期

基金：

中国国家自然科学基金;

关键词：

ZnNb2O6; Crystal growth; X-ray diffraction; Optical properties; LUMINESCENT PROPERTIES; COLUMBITE STRUCTURE; GROWTH; NIOBATES; PHOTOLUMINESCENCE; NANOCRYSTALS; 48-DEGREES; SIZE;

D O I：

10.1002/crat.201400094

中图分类号：

O7 [晶体学];

学科分类号：

0702 ; 070205 ; 0703 ; 080501 ;

摘要：

By using an optical floating zone technology, orthorhombic columbit ZnNb2O6 single crystals are fabricated successfully. The as-prepared sample are blue and transparent rods of Phi 4 to 6 mm x L 48 mm and the biggest domain of Phi 4 mm x L 25 mm. After annealing, the sample fades to colorless. X-ray diffractions indicates that the as-perpared samples are ZnNb2O6 with orthorhombic columbite structure and grows along the a-axis. The micropolariscopy in cross transmission arrangements analyzing give that the crystals are of low-angle crystal boundary-free and bubble-free. Besides, the crystals have also been tested by Raman spectra, optical absorption and photoluminescence spectra before and after being annealed. The luminescence pattern has an emission peak located at 450 nm blue-region.

引用

页码：502 / 506

页数：5

共 25 条

[1] CZOCHRALSKI GROWTH IN ZINC OXIDE-NIOBIUM PENTOXIDE SYSTEM [J].

BALLMAN, AA ;

BROWN, H .

JOURNAL OF CRYSTAL GROWTH, 1977, 41 (01) :36-40

[2] Fergusonite-type CeNbO4+δ: Single crystal growth, symmetry revision and conductivity [J].

Bayliss, Ryan D. ;

Pramana, Stevin S. ;

An, Tao ;

Wei, Fengxia ;

Kloc, Christian L. ;

White, Andrew J. P. ;

Skinner, Stephen J. ;

White, Timothy J. ;

Baikie, Tom .

JOURNAL OF SOLID STATE CHEMISTRY, 2013, 204 :291-297

[3] THE INFLUENCE OF STRUCTURAL DISORDER ON THE LUMINESCENCE OF NIOBATES - SCANDIUM NIOBATE (SCNBO4) AND MAGNESIUM NIOBATE (MGNB2O6) [J].

BLASSE, G ;

DIRKSEN, GJ ;

BRIXNER, LH .

MATERIALS CHEMISTRY AND PHYSICS, 1986, 14 (05) :485-494

[4] Quantum Criticality in an Ising Chain: Experimental Evidence for Emergent E8 Symmetry [J].

Coldea, R. ;

Tennant, D. A. ;

Wheeler, E. M. ;

Wawrzynska, E. ;

Prabhakaran, D. ;

Telling, M. ;

Habicht, K. ;

Smeibidl, P. ;

Kiefer, K. .

SCIENCE, 2010, 327 (5962) :177-180

[5] FLUX GROWTH OF MNB2O6 (M=MG,ZN,BA) SINGLE-CRYSTALS [J].

GREENBLATT, M ;

WANKLYN, BM ;

GARRARD, BJ .

JOURNAL OF CRYSTAL GROWTH, 1982, 58 (02) :463-466

[6] High-speed float zone growth of rutile single crystals inclined at 48° to the c-axis [J].

Higuchi, M ;

Sato, C ;

Kodaira, K .

JOURNAL OF CRYSTAL GROWTH, 2004, 269 (2-4) :342-346

[7] Floating-zone growth of rutile single crystals inclined at 48° to the c-axis [J].

Higuchi, M ;

Hatta, K ;

Takahashi, J ;

Kodaira, K ;

Kaneda, H ;

Saito, J .

JOURNAL OF CRYSTAL GROWTH, 2000, 208 (1-4) :501-507

[8] Photoluminescence and preparation of ZnNb2O6 doped with Eu3+ and Tm3+ nanocrystals for solar cell [J].

Hsiao, Yu-Jen ;

Fang, Te-Hua ;

Ji, Liang-Wen .

MATERIALS CHEMISTRY AND PHYSICS, 2011, 130 (03) :1187-1190

[9] Synthesis and luminescent properties of ZnNb2O6 nanocrystals for solar cell [J].

Hsiao, Yu-Jen ;

Fang, Te-Hua ;

Ji, Liang-Wen .

MATERIALS LETTERS, 2010, 64 (23) :2563-2565

[10] Synthesis and the luminescent properties of CdNb2O6 oxides by sol-gel process [J].

Hsiao, Yu-Jen ;

Chang, Yee-Shin ;

Chen, Guo-Ju ;

Chang, Yen-Hwei .

JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 471 (1-2) :259-262

← 1 2 3 →