Microstructural evolution and mechanical properties of Sn-Bi-Cu ternary eutectic alloy produced by directional solidification

被引:0
作者
Sahin, Mevlut [1 ]
Sensoy, Tolga [2 ]
Cadirli, Emin [3 ]
机构
[1] Nigde Omer Halisdemir Univ, Tech Vocat Sch Sci, Dept Elect & Automat, Nigde, Turkey
[2] Nigde Omer Halisdemir Univ, Inst Sci & Technol, Dept Phys, Nigde, Turkey
[3] Nigde Omer Halisdemir Univ, Fac Arts & Sci, Dept Phys, Nigde, Turkey
来源
MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS | 2018年 / 21卷 / 02期
关键词
Directional solidification; eutectic alloy; microstructure; intermetallic compound; microhardness; compressive strength; LEAD-FREE SOLDERS; TENSILE PROPERTIES; INTERMETALLIC COMPOUNDS; RAPID SOLIDIFICATION; FATIGUE PROPERTIES; AG-CU; BEHAVIOR; PARAMETERS; MORPHOLOGY; CU6SN5;
D O I
10.1590/1980-5373-MR-2017-0901
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Sn-36Bi-22Cu (wt.%) ternary eutectic alloy was prepared using vacuum melting furnace and casting furnace. The samples were directionally solidified upwards solidification rate varying from 8.3 to 166 mu m/s and at a constant temperature gradient (4.2 K/mm) in a Bridgman-type directional solidification furnace. The composition analysis of the phases and the intermetallics (Cu3Sn and Cu6Sn5) were determined from EDX and XRD analysis respectively. The variation of the lamellar spacing (Bi-rich phase) and the Cu3Sn phase spacing with the solidification rate were investigated. The dependence of microhardness, ultimate compressive strength and compressive yield strength on solidification rate were determined. The spacing and microhardness were measured from both longitudinal and transverse sections of the samples. The dependence of microhardness on the lamellar spacing and the Cu3Sn phase spacing were also determined. The relationships between phase spacings, solidification rate and mechanical properties were determined from linear regression analysis.
引用
收藏
页数:10
相关论文
共 59 条
[1]   Microstructure, tensile properties and wear resistance correlations on directionally solidified Al-Sn-(Cu; Si) alloys [J].
Bertelli, Felipe ;
Freitas, Emmanuelle S. ;
Cheung, Noe ;
Arenas, Maria A. ;
Conde, Ana ;
de Damborenea, Juan ;
Garcia, Amauri .
JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 695 :3621-3631
[2]   Critical interlayer thickness for transient liquid phase bonding in the Cu-Sn system [J].
Bosco, NS ;
Zok, FW .
ACTA MATERIALIA, 2004, 52 (10) :2965-2972
[3]   Characterization of a Directionally Solidified Sn–Pb–Sb Ternary Eutectic Alloy [J].
Çadırlı E. ;
Şahin M. ;
Turgut Y. .
Metallography, Microstructure, and Analysis, 2015, 4 (04) :286-297
[4]  
Campbell J., 1981, International Metals Reviews, V26, P71
[5]   The solidus line of the Cu-Bi phase diagram [J].
Chang, LS ;
Straumal, BB ;
Rabkin, E ;
Gust, W ;
Sommer, F .
JOURNAL OF PHASE EQUILIBRIA, 1997, 18 (02) :128-135
[6]  
Chen Z, 2014, THESIS
[7]   Strain- and strain-rate-dependent mechanical properties and behaviors of Cu3Sn compound using molecular dynamics simulation [J].
Cheng, Hsien-Chie ;
Yu, Ching-Feng ;
Chen, Wen-Hwa .
JOURNAL OF MATERIALS SCIENCE, 2012, 47 (07) :3103-3114
[8]   Interdiffusion and phase formation in Cu(Sn) alloy films [J].
Clevenger, LA ;
Arcot, B ;
Ziegler, W ;
Colgan, EG ;
Hong, QZ ;
d'Heurle, FM ;
Cabral, C ;
Gallo, TA ;
Harper, JME .
JOURNAL OF APPLIED PHYSICS, 1998, 83 (01) :90-99
[9]   Deformation behavior of (Cu, Ag)-Sn intermetallics by nanoindentation [J].
Deng, X ;
Chawla, N ;
Chawla, KK ;
Koopman, M .
ACTA MATERIALIA, 2004, 52 (14) :4291-4303
[10]   Influence of initial morphology and thickness of Cu6Sn5 and Cu3Sn intermetallics on growth and evolution during thermal aging of Sn-Ag solder/Cu joints [J].
Deng, X ;
Piotrowski, G ;
Williams, JJ ;
Chawla, N .
JOURNAL OF ELECTRONIC MATERIALS, 2003, 32 (12) :1403-1413