Effect of Corrosion on the Fatigue Life of Aged EMU under Fatigue Loading

被引:7
作者
Jun, Hyun-Kyu [1 ]
Seo, Jung-Won [1 ]
Kwon, Seok-Jin [1 ]
Lee, Dong-Hyung [1 ]
Park, Sung-Hyuk [2 ]
机构
[1] Korea Railroad Res Inst, Fatigue & Fracture Res Team, 176 Cheoldobangmulgwan Ro, Uiwang Si 16105, Gyeonggi Do, South Korea
[2] Korea Railroad Res Inst, Railrd Safety & Certificat Ctr, 176 Cheoldobangmulgwan Ro, Uiwang Si 16105, Gyeonggi Do, South Korea
关键词
Corrosion; Fatigue life; Railway car-body; Underframe; Aged electric multiple unit;
D O I
10.1007/s12541-016-0010-3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
It is very useful to know in advance the remaining life of long life span structure for the reasons of safety assurance or setting up cost effective overhaul strategy. A railroad car is designed to have a very long life span over 40 years, and therefore corrosion and fatigue damage on the major components of the structure are known to big problems. The fatigue damage is accelerated with the growth of corrosion due to the falling-off in strength. For this reason, the railroad industry performs diagnosis of the remaining life of aged railroad cars considering fatigue and corrosion effects on the structure. In this study, the remaining fatigue life of aged railroad cars was calculated by considering the effectivity of corrosion on the static and dynamic strength of the car-body For this purpose, a series of finite element analyses was performed to quantify) the effectivity of corrosion. And the results were implemented for the fatigue life prediction of aged car bodies. The fatigue life was reduced by about 20% at the corrosion thickness of 0.3 mm, the measured thickness on the 23 years aged car, and about 40% at the corrosion thickness of 0.72 mm, the predicted thickness on the 40 years aged car, compared to the base thickness of the car-body. Therefore it can be concluded that consideration of the corrosion effect is very important in prediction of the remaining fatigue life.
引用
收藏
页码:73 / 79
页数:7
相关论文
共 50 条
  • [41] A conversion approach for predicting the fatigue life of structures under multiple loading conditions
    Tang, Qinghong
    Ma, Jisheng
    Li, Zhiqiang
    MULTISCALING ASSOCIATED WITH STRUCTURAL AND MATERIAL INTEGRITY UNDER ELEVATED TEMPERATURE, 2006, : 253 - 257
  • [42] Application of the covariance on the critical plane for determination of fatigue life under cyclic loading
    Walat, Karolina
    Lagoda, Tadeusz
    FATIGUE 2010, 2010, 2 (01): : 1211 - 1218
  • [43] Fatigue Life Numerical Prediction of Butt Welded Plate Under Cyclic Loading
    Wang, Yifei
    Qu, Weilian
    Zhao, Ernian
    Ji, Baifeng
    Wang, Liang
    CIVIL, STRUCTURAL AND ENVIRONMENTAL ENGINEERING, PTS 1-4, 2014, 838-841 : 265 - 269
  • [44] Reliability-based fatigue life of vehicle spring under random loading
    Manouchehry Nya, Reza
    Abdullah, Shahrum
    Singh Karam Singh, Salvinder
    INTERNATIONAL JOURNAL OF STRUCTURAL INTEGRITY, 2019, 10 (05) : 737 - 748
  • [45] Effect of Loading Parameter on Fretting Fatigue
    Kowser, Md. Arefin
    Chowdhury, Mohammad Asaduzzaman
    Shah, Md. Zobaer
    7TH BSME INTERNATIONAL CONFERENCE ON THERMAL ENGINEERING (ICTE), 2017, 1851
  • [46] Corrosion fatigue effects on life estimation of deteriorated bridges under vehicle impacts
    Zhang, W.
    Yuan, H.
    ENGINEERING STRUCTURES, 2014, 71 : 128 - 136
  • [47] Effect of the Nut Position Changings on the Fatigue Life of the Stud-Nut Connection under Cyclic Axial Loading
    Selivonec, J.
    Krenevicius, A.
    MECHANIKA 2015: PROCEEDINGS OF THE 20TH INTERNATIONAL SCIENTIFIC CONFERENCE, 2015, : 230 - 234
  • [48] Deterioration of fatigue strength of bolted connection plates under combined corrosion and fatigue
    Li, Le
    Li, Yueru
    Shi, Wenhai
    Li, Chun-Qing
    JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2021, 179
  • [49] Under the corrosion in sodium fatigue performance of concrete
    Zhou, Jinghai
    Wang, Weiwei
    Meng, Xianhong
    ADVANCES IN STRUCTURAL ENGINEERING, PTS 1-3, 2011, 94-96 : 1180 - +
  • [50] The effect of repetitive magnetic and cyclic loading on the fatigue life prediction of a magnetorheological elastomer
    Hosseini, Seyyed Mohammad
    Shojaeefard, Mohammad Hassan
    Googarchin, Hamed Saeidi
    JOURNAL OF ELASTOMERS AND PLASTICS, 2022, 54 (02) : 279 - 299