Properties of volcanic scoria based lightweight concrete

被引：29
作者：
Hossain, KMA [1 ]
机构：
[1] Ryerson Univ, Dept Civil Engn, Toronto, ON M5B 2K3, Canada
来源：
MAGAZINE OF CONCRETE RESEARCH | 2004年 / 56卷 / 02期
关键词：
D O I：
10.1680/macr.56.2.111.36296
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
The results of investigations on the suitability of using volcanic scoria (VS) as coarse aggregate in lightweight concrete production are reported. Tests were conducted on concrete by replacing 0-100% of coarse crushed gravel aggregate by volume. The physical properties of volcanic scoria were critically reviewed to evaluate the possible influence on both the fresh and hardened state of concrete. The properties of VS concrete using different percentages of VS aggregate were evaluated by conducting a comprehensive series of tests on workability, strength, drying shrinkage, surface absorption and water permeability. It is concluded that the VS concrete has sufficient strength and adequate density to be accepted as structural lightweight concrete. However, compared with the control concrete, the VS concrete has a lower modulus of elasticity, and higher permeability and initial surface absorption.
引用
收藏
页码：111 / 120
页数：10
相关论文
共 40 条
[1]  
*ACI COMM 301, 1975, J AM CONCRETE I, V72, P361
[2]   Effect of initial curing on early strength and physical properties of a lightweight concrete [J].
Al-Khaiat, H ;
Haque, MN .
CEMENT AND CONCRETE RESEARCH, 1998, 28 (06) :859-866
[3]  
*AM CONCR I, 1989, 221R89 ACI
[4]  
*AM SOC TEST MAT, 2000, 3797 BSI BS
[5]  
*AM SOC TEST MAT, 1999, 15799 ASTM C
[6]  
*AM SOC TEST MAT, 2000, 61800 ASTM C
[7]  
*AM SOC TEST MAT, 2000, 14300 ASTM C
[8]  
*AM SOC TEST MAT, 1997, 14297 ASTM C
[9]  
*AM SOC TEST MAT, 2000, 31100 ASTM C
[10]  
*AM SOC TEST MAT, 2001, 13601 ASTM C
1234