Effect of sintering aids on the densification of andalusite ceramics

被引：1

作者：

Wu, Jianfeng ^{[1
]}

Cheng, Hao ^{[1
]}

Xu, Xiaohong ^{[1
]}

Deng, Tengfei ^{[1
]}

机构：

[1] State Key Lab Silicate Mat Architectures, Wuhan 430070, Peoples R China

来源：

MATERIALS, MECHANICAL AND MANUFACTURING ENGINEERING | 2014年 / 842卷

关键词：

andalusite; mullite; sintering aid; densification; ALUMINA; KAOLIN; POWDER;

D O I：

10.4028/www.scientific.net/AMR.842.78

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The ceramics with large bulk density and high bending strength were fabricated via semi-dry pressing and pressureless sintering in the air. Andalusite and calcined bauxite were used as the raw materials, sintering aids such as potassium feldspar, albite, talc, spodumene and borax were added to promote the densification and decrease the sintering temperature of the samples. The best physical properties were obtained on a sample of optimal composition (the addition of sintering aid was talc) sintered at 1500 degrees C for 3 h, i.e. a bending strength of 138.52 MPa and bulk density of 2.61g.cm(-3), the sintering temperature was lower than sample without addition of sintering aid.

引用

页码：78 / 82

页数：5

共 12 条

[1] Microstructure and thermal cycle resistance of plasma sprayed mullite coatings made from secondary mullitized natural andalusite powder [J].

An, Yulong ;

Chen, Jianmin ;

Zhou, Huidi ;

Liu, Guang .

SURFACE & COATINGS TECHNOLOGY, 2010, 205 (07) :1897-1903

[2]

Bouchetou M.L., 2009, REFRACT APPL, V14, P14

[3]

Bouchetou M.L., 2005, REFRACTORIES APPL NE, V10, P21

[4] Mullite whiskers derived from kaolin [J].

Kim, B. M. ;

Cho, Y. K. ;

Yoon, S. Y. ;

Stevens, R. ;

Park, H. C. .

CERAMICS INTERNATIONAL, 2009, 35 (02) :579-583

[5] KINETIC-ANALYSIS OF SOLUTION-PRECIPITATION DURING LIQUID-PHASE SINTERING OF ALUMINA [J].

KWON, OH ;

MESSING, GL .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (02) :275-281

[6] Preparation of short mullite fibers from kaolin via the addition of foaming agents [J].

Li, KQ ;

Shimizu, T ;

Igarashi, K .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2001, 84 (03) :497-503

[7] EFFECT OF ACTIVE ALUMINA ON SINTERING BEHAVIOR OF ANDALUSITE POWDER [J].

Li, Liusheng ;

Cao, Qincun ;

Xu, Guohui ;

Liao, Guihua .

APPLICATIONS OF ENGINEERING MATERIALS, PTS 1-4, 2011, 287-290 :1003-+

[8] Manufacture of mullite substrates from andalusite for the development of thin film solar cells [J].

Mazel, F ;

Gonon, M ;

Fantozzi, G .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (04) :453-461

[9]

Rebouillat L, 2002, J AM CERAM SOC, V85, P373

[10]

Singh VK., 1981, J AM CERAM SOC, V64, pC, DOI [10.1111/j.1151-2916.1981.tb10235.x, DOI 10.1111/J.1151-2916.1981.TB10235.X]

← 1 2 →