FATIGUE CRACK INITIATION MODEL OF TYPE 316 STAINLESS STEEL

被引：0
|
作者：
Ishizawa, Terushi [1 ]
Nakamura, Takao [1 ]
Kitada, Takanori [1 ]
机构：
[1] Osaka Univ, 2-1 Yamadaoka Suita, Osaka 5650871, Japan
来源：
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, 2016, VOL 5 | 2017年
关键词：
GROWTH;
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The fatigue tests under different conditions of strain range were conducted in air and the replica observation of fatigue cracks on specimen surface was also conducted. Using data obtained in fatigue tests, statistical dispersion of crack initiation life was quantified and modeled through an application of two parameter Weibull distribution. The relationship between strain range and two parameters (s, shape parameter and eta, scale parameter) of crack initiation model was discussed. Thereby, the applicability of crack initiation model for arbitrary strain range was shown. Furthermore, the validation of P-curve applied crack initiation model was conducted by the simulation of fatigue life.
引用
收藏
页数：7
相关论文
共 50 条
  • [21] FATIGUE CRACK INITIATION AND GROWTH IN STAINLESS STEEL PIPE WELDS
    Green, D.
    Smith, R. D.
    Taggart, J. P.
    Beardsmore, D.
    Robinson, S.
    ASME PRESSURE VESSELS AND PIPING CONFERENCE 2009, VOL 3: DESIGN AND ANALYSIS, 2010, : 557 - 566
  • [22] FATIGUE CRACK INITIATION AND GROWTH OBSERVATION FOR 316 STAINLESS STEEL SUBJECTED TO EQUI-BIAXIAL CYCLIC LOADING
    Iida, Satohi
    Abe, Shigeki
    Nakamura, Takao
    Kamaya, Masayuki
    ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2015, VOL 3, 2015,
  • [23] FATIGUE-CRACK INITIATION AND PROPAGATION ON SHOT-PEENED SURFACES IN A316 STAINLESS-STEEL
    DELOSRIOS, ER
    WALLEY, A
    MILAN, MT
    HAMMERSLEY, G
    INTERNATIONAL JOURNAL OF FATIGUE, 1995, 17 (07) : 493 - 499
  • [24] Short fatigue crack behaviour in 316L stainless steel
    Obrtlik, K
    Polak, J
    Hajek, M
    Vasek, A
    INTERNATIONAL JOURNAL OF FATIGUE, 1997, 19 (06) : 471 - 475
  • [25] Non-destructive evaluation of fatigue damage and fatigue crack initiation in type 316 stainless steel by positron annihilation line-shape and lifetime analyses
    Uematsu, Y.
    Kakiuchi, T.
    Hattori, K.
    Uesugi, N.
    Nakao, F.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (07) : 1143 - 1153
  • [26] EFFECT OF CARBIDE PRECIPITATION ON FATIGUE CRACK-PROPAGATION IN TYPE-316 STAINLESS-STEEL
    MAHONEY, MW
    PATON, NE
    NUCLEAR TECHNOLOGY, 1974, 23 (01) : 53 - 62
  • [27] Effect of Environment on Fatigue Crack Growth Behavior of Type 316 LN Stainless Steel and its Weldments
    Poonguzhali, A.
    Babu, M. Nani
    Ravi, S.
    Ningshen, S.
    Amarendra, G.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2022, 31 (05) : 3918 - 3929
  • [28] FATIGUE CRACK-PROPAGATION IN TYPE-316 STAINLESS-STEEL AT ELEVATED-TEMPERATURES
    SMITH, HH
    MICHEL, DJ
    REPORT OF NRL PROGRESS, 1976, (OCT): : 7 - 8
  • [29] FATIGUE CRACK GROWTH RATES IN TYPE 316 STAINLESS STEEL AT ELEVATED TEMPERATURE AS A FUNCTION OF OXYGEN PRESSURE
    SMITH, HH
    SHAHINIA.P
    ACHTER, MR
    JOURNAL OF METALS, 1969, 21 (03): : A31 - &
  • [30] FATIGUE CRACK-GROWTH IN THIN-SECTION TYPE-316 STAINLESS-STEEL
    RICKERBY, DG
    FENICI, P
    ENGINEERING FRACTURE MECHANICS, 1984, 19 (04) : 585 - 599
12345