Processing maps for the analysis of hot workability of microalloyed steels 38MnSiVS5 and 0.39C1.47Mn

被引:12
作者
da Silva Septimio, Rudimylla [1 ]
Button, Sergio Tonini [1 ]
Van Tyne, Chester John [2 ]
机构
[1] Univ Estadual Campinas, Sch Mech Engn, BR-13083970 Campinas, SP, Brazil
[2] Colorado Sch Mines, Dept Met & Mat Engn, Golden, CO 80401 USA
基金
巴西圣保罗研究基金会;
关键词
HIGH-STRENGTH STEELS; STRAIN-RATE; INSTABILITY CRITERIA; FLOW BEHAVIOR; DEFORMATION; PRECIPITATION; NB; RECRYSTALLIZATION; IDENTIFICATION; COMPRESSION;
D O I
10.1007/s10853-015-9563-2
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Microalloyed steels are gaining increasing importance as substitutions for carbon steels because they possess higher mechanical properties, such as strength and toughness after hot forging, without a need for post-deformation heat treatment. To increase machinability, sulfur is added to microalloyed steels to facilitate chip removal, increase productivity, and enhance the life of cutting tools. Otherwise, the sulfide particles that benefit machinability may cause a significant loss in hot workability. Therefore, it is important to understand the effect of initial grain size, phase constituents, and inclusion content on flow stresses during hot working in order to establish ideal processing conditions, which prevent the formation of defects and simultaneously improve mechanical properties. The aim of the current study is to construct processing maps to evaluate the hot workability of microalloyed steels DIN 38MnSiVS5 and 0.39C1.47Mn in order to define the constitutive behavior of both steels under hot working and identify the safe regions for metalworking. The processing maps for both steels showed a region of instability at temperatures between 1100 and 1150 A degrees C and the highest strain rates (namely, 10.0 and 30.0 s(-1)) that should be avoided. Cracks were found in the sample of 0.39C1.47Mn steel and voids were found in the central region in the DIN 38MnSiVS5 steel. These defects might be caused by MnS inclusions and are probably the cause of instability. Therefore, it can be concluded that a higher sulfur content has a negative effect on workability, and might be the cause of instability under some processing conditions.
引用
收藏
页码:2512 / 2528
页数:17
相关论文
共 36 条
[1]  
Bramfitt B.L., 2001, Metallographer's Guide: Practice and Procedures for Irons and Steels
[2]   Influence of cooling rate on the precipitation behavior in Ti-Nb-Mo microalloyed steels during continuous cooling and relationship to strength [J].
Bu, F. Z. ;
Wang, X. M. ;
Chen, L. ;
Yang, S. W. ;
Shang, C. J. ;
Misra, R. D. K. .
MATERIALS CHARACTERIZATION, 2015, 102 :146-155
[3]   Effects of Sulfur Level and Anisotropy of Sulfide Inclusions on Tensile, Impact, and Fatigue Properties of SAE 4140 Steel [J].
Cyril, Nisha ;
Fatemi, Ali ;
Cryderman, Bob .
SAE INTERNATIONAL JOURNAL OF MATERIALS AND MANUFACTURING, 2009, 1 (01) :218-227
[4]   Characterization of deformation stability of medium carbon microalloyed steel during hot forging using phenomenological and continuum criteria [J].
El Hassani, F. Bakkali ;
Chenaouia, A. ;
Dkiouak, R. ;
Elbakkali, L. ;
Al Omar, A. .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 199 (1-3) :140-149
[5]   Constitutive Modeling of Dynamic Recrystallization Behavior and Processing Map of 38MnVS6 Non-Quenched Steel [J].
Gu, Sen-dong ;
Zhang, Li-wen ;
Ruan, Jin-hua ;
Zhou, Ping-zhen ;
Zhen, Yu .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (03) :1062-1068
[6]   Improvement in Mechanical Properties of Microalloyed Steel 30MSV6 by a Precipitation Hardening Process [J].
Hajisafari, M. ;
Nategh, S. ;
Yoozbashizadeh, H. ;
Ekrami, A. .
JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2013, 20 (05) :66-73
[7]   Study of the strain reversal effect on the recrystallization and strain-induced precipitation in a Nb-microalloyed steel [J].
Jorge-Badiola, D ;
Gutiérrez, I .
ACTA MATERIALIA, 2004, 52 (02) :333-341
[8]  
Kim KW, 2015, J MATER SCI, V18, P641, DOI [10.1016/s10853-015-9171-1, DOI 10.1016/S10853-015-9171-1]
[9]   Hot Ductility of Sulfur-containing Low Manganese Mild Steels at High Strain Rate [J].
Kizu, Taro ;
Urabe, Toshiaki .
ISIJ INTERNATIONAL, 2009, 49 (09) :1424-1431
[10]  
Lenz M, 2014, J MATER SCI, V49, P1121, DOI [10.1007/s10853-013-7790-y, DOI 10.1007/S10853-013-7790-Y]