Effect of Calcination Conditions on Crystalline Structure and Pore Size Distribution for a Mesoporous Alumina

被引：22

作者：

Ravanchi, Maryam Takht ^{[1
]}

Fard, Maryam Rahimi ^{[1
]}

Rayeeni, Siyavash Fadaee ^{[1
]}

Yaripour, Fereidoon ^{[1
]}

机构：

[1] Natl Petrochem Co, Petrochem Res & Technol Co, Catalyst Res Grp, Tehran, Iran

来源：

CHEMICAL ENGINEERING COMMUNICATIONS | 2015年 / 202卷 / 04期

关键词：

Pore size distribution; Alumina; Calcination temperature; Crystalline structure; ALPHA-PHASE TRANSFORMATION; THETA-PHASE; SEEDED BOEHMITE; ALPHA-AL2O3; GROWTH; TRANSITION; POWDERS; GEL; PARTICLES; EVOLUTION;

D O I：

10.1080/00986445.2013.850577

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

In this article, a mesoporous commercial alumina was calcined in the temperature range of 600 degrees C-1200 degrees C. The effect of several parameters such as calcination temperature, calcination time, heating rate, and calcination steps on phase transformation and crystal size was experimentally investigated. The characterization of the commercial mesoporous alumina and samples calcined at 1000 degrees C, 1040 degrees C, 1070 degrees C, 1100 degrees C, and 1200 degrees C by single-step and multi-step calcination was performed using XRD and N-2 adsorption/desorption techniques. For the commercial mesoporous alumina, TG/DTA analysis was also performed. Experimental results showed that mostly pure alpha-Al2O3 was obtained at 1100 degrees C.

引用

页码：493 / 499

页数：7

共 50 条

[1] Effects of calcination temperature on the pore size and wall crystalline structure of mesoporous alumina
Sun, Zhong-Xi
Zheng, Ting-Ting
Bo, Qi-Bing
Du, Miao
Forsling, Willis
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2008, 319 (01) : 247 - 251
[2] EFFECT OF ACIDIC AND BASIC VAPORS ON PORE-SIZE DISTRIBUTION OF ALUMINA UNDER HYDROTHERMAL CONDITIONS
ABSIHALABI, M
STANISLAUS, A
ALZAID, H
APPLIED CATALYSIS A-GENERAL, 1993, 101 (01) : 117 - 128
[3] Effect of flocculation of alumina slip on the pore size distribution of cast alumina by polyacrylamide (PAM)
Silakate, Piamchit
Nuntiya, Apinon
Larpkiattaworn, Siriporn
CHIANG MAI JOURNAL OF SCIENCE, 2008, 35 (01): : 17 - 22
[4] Analysis of Crystalline Structure of Sodium Tripolyphosphate: Effect of pH of Solution and Calcination Conditions
Sadeghi, F.
Fayazi, A.
INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2012, 51 (03) : 1093 - 1098
[5] Effect of Mixing on the Pore Structure of Alumina Extrudates
Landers, John
Devadas, Mukundan
Neimark, Alexander V.
Timken, Hye-Kyung
Ojo, Adeola
Chester, Arthur W.
PARTICLE & PARTICLE SYSTEMS CHARACTERIZATION, 2010, 27 (1-2) : 42 - 47
[6] Preparation and characterisation of mesoporous silica-alumina and silica-titania with a narrow pore size distribution
Carati, A
Ferraris, G
Guidotti, M
Moretti, G
Psaro, R
Rizzo, C
CATALYSIS TODAY, 2003, 77 (04) : 315 - 323
[7] Synthesis of ordered mesoporous γ-alumina - Effects of calcination conditions and polymeric template concentration
Taromi, Arsia Afshar
Kaliaguine, Serge
MICROPOROUS AND MESOPOROUS MATERIALS, 2017, 248 : 179 - 191
[8] Preparation of alumina with high specific surface area and narrow pore size distribution I. Effect of precipitation conditions
Du, MX
Zhai, XZ
Li, Y
Li, LD
Zhu, HQ
Tan, CY
CHINESE JOURNAL OF CATALYSIS, 2002, 23 (05) : 465 - 468
[9] Synthesis and properties of mesoporous silica-alumina with narrow pore size distribution obtained without use of pore-regulating agents
Vit, Zdenek
Solcova, Olga
MICROPOROUS AND MESOPOROUS MATERIALS, 2006, 96 (1-3) : 197 - 204
[10] Molecular model of γ-alumina:: Nitrogen adsorption and pore size distribution
Figueroa-Gerstenmaier, S
Vega, LF
Blas, FJ
Gubbins, KE
FOUNDATIONS OF MOLECULAR MODELING AND SIMULATION, 2001, 97 (325): : 317 - 320

← 1 2 3 4 5 →