Relationship between microstructure and mechanical properties of TiAl/Ti2AlNb joint brazed using Ti-27Co eutectic filler metal

被引：51

作者：

Cao, Jian ^{[1
]}

Dai, Xiangyu ^{[1
]}

Liu, Jiaqi ^{[1
]}

Si, Xiaoqing ^{[1
]}

Feng, Jicai ^{[1
]}

机构：

[1] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China

来源：

MATERIALS & DESIGN | 2017年 / 121卷

基金：

中国国家自然科学基金;

关键词：

TiAI alloy; Ti2AlNb alloy; Brazing; Interfacial microstructure; Nano-indentation; BRAZING HIGH NB; TIAL ALLOY; HEAT-TREATMENT; PHASE; CO; TEMPERATURE; POWDER; EVOLUTION;

D O I：

10.1016/j.matdes.2017.02.067

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Partially substituting TiAl alloys for Ti(2)AINb alloys has been identified as an effective approach to realize the weight reduction of aircraft engines. Therefore, joining of TiAl alloy to Ti2AlNb alloy is important and meaningful. In this study, TiAI alloy and Ti2AlNb alloy were successfully brazed at 1080-1140 degrees C for 10 min using Ti-27Co (wt%) eutectic filler metal. Scanning electron microscope (SEM), energy dispersive spectrometer (EDS) and transmission electron microscope (TEM) were employed to characterize the interfacial microstructure of the joints. The results showed that alpha(2)-Ti3Al, beta-Ti, TiCo, Ti2Co and B-2 phases were formed in the brazing seam of the joints. As the brazing temperature increased, the thickness of diffusion layer in the TiAl side became thicker correspondingly. Higher brazing temperature accelerated the diffusion of Co element into the substrates, resulting in the disappearance of band-like Ti2Co phase and the growth of acicular Ti3Al phase. The highest shear strength of the joints was 223 MPa when brazed at 1100 degrees C for 10 min. The hardness and elastic modulus of the phases in the joint were measured by nano-indentation to show the plastic deformation capacity. In addition, the microstructure evolution mechanism of the joints was put forward based on the experimental analysis. (C) 2017 Elsevier Ltd. All rights reserved.

引用

页码：176 / 184

页数：9

共 38 条

[11] Vacuum brazing of TiAl alloy to 40Cr steel with Ti60Ni22Cu10Zr8 alloy foil as filler metal [J].

Dong, Honggang ;

Yang, Zhonglin ;

Yang, Guoshun ;

Dong, Chuang .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 561 :252-258

[12] Microstructure characterization and mechanical behaviors of a hot forged high Nb containing PM-TiAl alloy [J].

Li, Jianbo ;

Liu, Yong ;

Liu, Bin ;

Wang, Yan ;

Liang, Xiaopeng ;

He, Yuehui .

MATERIALS CHARACTERIZATION, 2014, 95 :148-156

[13] Effects of brazing temperature and testing temperature on the microstructure and shear strength of γ-TiAl joints [J].

Li, Li ;

Li, Xiaoqiang ;

Hu, Me ;

Qu, Shengguan ;

Yang, Chao ;

Li, Zhifeng .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 634 :91-98

[14] Vacuum brazing of TiAl-based intermetallics with Ti-Zr-Cu-Ni-Co amorphous alloy as filler metal [J].

Li, Xiaoqiang ;

Li, Li ;

Hu, Ke ;

Qu, Shengguan .

INTERMETALLICS, 2015, 57 :7-16

[15] The effect of postproduction heat treatment on γ-TiAl alloys produced by the GTAW-based additive manufacturing process [J].

Ma, Yan ;

Cuiuri, Dominic ;

Li, Huijun ;

Pan, Zengxi ;

Shen, Chen .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 657 :86-95

[16] Microstructure and mechanical properties of Al2O3 ceramic and TiAl alloy joints brazed with Ag-Cu-Ti filler metal [J].

Niu, G. B. ;

Wang, D. P. ;

Yang, Z. W. ;

Wang, Y. .

CERAMICS INTERNATIONAL, 2016, 42 (06) :6924-6934

[17] Fabrication of a powder metallurgy Ti2AlNb-based alloy by spark plasma sintering and associated microstructure optimization [J].

Niu, H. Z. ;

Chen, Y. F. ;

Zhang, D. L. ;

Zhang, Y. S. ;

Lu, J. W. ;

Zhang, W. ;

Zhang, P. X. .

MATERIALS & DESIGN, 2016, 89 :823-829

[18] A first principles study of Ti2AlNb intermetallic [J].

Pathak, Ashish ;

Singh, A. K. .

SOLID STATE COMMUNICATIONS, 2015, 204 :9-15

[19] Microstructure and mechanical properties of TiAl alloy joints vacuum brazed with Ti-Zr-Ni-Cu brazing powder without and with Mo additive [J].

Qiu, Qiwen ;

Wang, Ying ;

Yang, Zhenwen ;

Hu, Xin ;

Wang, Dongpo .

MATERIALS & DESIGN, 2016, 90 :650-659

[20] Vacuum brazing of Ti3Al-based alloy to TiAl using TiZrCuNi(Co) fillers [J].

Ren, H. S. ;

Xiong, H. P. ;

Chen, B. ;

Pang, S. J. ;

Chen, B. Q. ;

Ye, L. .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2015, 224 :26-32

← 1 2 3 4 →