Oxidation-induced crack healing in Zr2Al4C5 ceramic

被引：20
|
作者：
Chen, Guiqing [1 ]
Zhang, Rubing [1 ]
Zhang, Xinghong [1 ]
Zhao, Lei [1 ]
Han, Wenbo [1 ]
机构：
[1] Harbin Inst Technol, Ctr Composite Mat, Harbin 150001, Peoples R China
来源：
MATERIALS & DESIGN | 2009年 / 30卷 / 09期
基金：
中国国家自然科学基金;
关键词：
Crack healing; Flexural strength; Oxidation; REINFORCED ALUMINA; SILICON-NITRIDE; BEHAVIOR; CARBIDE; COMPOSITES; INTEGRITY; STRENGTH; TI3ALC2; AIR;
D O I：
10.1016/j.matdes.2009.02.024
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The crack-healing behavior of Zr2Al4C5 was investigated by oxidizing the pre-cracked sample. A Vickers indentation (similar to 80 mu m in size) was introduced and the crack was healed under different temperature. Cracks could heal completely in air above 1000 degrees C, with oxidation products consisting primarily of t-ZrO2 and alpha-Al2O3. The bending strength of crack-healed specimen (188-283 MPa) is higher than that of cracked samples (182 MPa), but all of them are lower than the strength of as-sintered and polished specimens (420 MPa). This composite has self crack-healing ability at temperatures ranging from 800 to 1200 degrees C, with 1000 degrees C being the optimum healing temperature. (C) 2009 Elsevier Ltd. All rights reserved.
引用
收藏
页码：3602 / 3607
页数：6
相关论文
共 50 条
  • [41] In situ synthesis and properties of Zr2Al3C4/ZrB2 composites
    Guo Qilong
    Yang Yahui
    Li Junguo
    Shen Qiang
    Zhang Lianmeng
    MATERIALS & DESIGN, 2011, 32 (8-9) : 4289 - 4294
  • [42] Oxidation and alpha-case formation in Ti-6Al-2Sn-4Zr-2Mo alloy
    Gaddam, Raghuveer
    Sefer, Birhan
    Pederson, Robert
    Antti, Marta-Lena
    MATERIALS CHARACTERIZATION, 2015, 99 : 166 - 174
  • [43] Oxidation behavior of a TiAl-Al2Ti4C2-TiC-Al2O3 in situ composite
    Li, Z
    Gao, W
    Zhang, DL
    Cai, ZH
    OXIDATION OF METALS, 2004, 61 (3-4): : 339 - 354
  • [44] Comparison of the dry and wet oxidation at 900 °C of η-Fe2Al5 and δ-Ni2Al3 coatings
    Zheng, L.
    Peng, X.
    Wang, F.
    CORROSION SCIENCE, 2011, 53 (02) : 597 - 603
  • [45] Oxidation-Induced Changes in the ALD-Al2O3/InAs(100) Interface and Control of the Changes for Device Processing
    Tuominen, Marjukka
    Makela, Jaakko
    Yasir, Muhammad
    Dahl, Johnny
    Granroth, Rsari
    Lehtio, Juha-Pekka
    Felix, Roberto
    Laukkanen, Pekka
    Kuzmin, Mikhail
    Laitinen, Mikko
    Punkkinen, Marko P. J.
    Hedman, Hannu-Pekka
    Punkkinen, Risto
    Polojarvi, Ville
    Lyytikainen, Jan
    Tukiainen, Antti
    Guina, Mircea
    Kokko, Kalevi
    ACS APPLIED MATERIALS & INTERFACES, 2018, 10 (51) : 44932 - 44940
  • [46] Structure and oxidation behaviors of C/C-SiC coated with Al2O3-CrAl0.42Si1.58-SiC-Al4SiC4 oxidation protection system
    Jiao Geng-Sheng
    Li He-Jun
    Lu Guo-Feng
    ADVANCED COMPOSITE MATERIALS, 2012, 21 (04) : 273 - 281
  • [47] Oxidation Behavior of a TiAl–Al2Ti4C2–TiC–Al2O3in situ Composite
    Z. Li
    W. Gao
    D. L. Zhang
    Z. H. Cai
    Oxidation of Metals, 2004, 61 : 339 - 354
  • [48] Microstructure, mechanical, and thermal properties of in situ-synthesized (ZrB2+SiC)/Zr2[Al(Si)]4C5 composites
    Guo, D. D.
    Yang, J.
    Yu, L.
    Pan, L. M.
    Qiu, T.
    Zhang, J. X.
    CERAMICS INTERNATIONAL, 2013, 39 (07) : 8559 - 8563
  • [49] More effective crack self-healing capability of SiCf/SiC-B4C with Al2O3modified under wet environment
    Shan, Qingliang
    Xue, Yudong
    Hu, Jianbao
    Xu, Qiankun
    Ma, Qian
    Zeng, Shenghui
    Lian, Jiawei
    Wang, Yewei
    Shui, Anze
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2020, 103 (12) : 7247 - 7258
  • [50] The crack-healing and strength recovery mechanisms for the new developed Ti(C,N)-TiSi2-WC composite ceramic tool materials with crack-healing ability
    Cui, Xinyao
    Huang, Chuanzhen
    Shi, Zhenyu
    Liu, Hanlian
    Li, Shijie
    Han, Youlong
    Ji, Lianggang
    Wang, Zhen
    Xu, Longhua
    Huang, Shuiquan
    CERAMICS INTERNATIONAL, 2023, 49 (22) : 35382 - 35391
12345