Corrosion study of a Zn-22Al-2Cu alloy coated withY2O3

被引：4

作者：

Guerrero, R

Farias, MH

Cota-Araiza, L

机构：

[1] Inst Tecnol Tijuana, Ctr Grad & Invest, Tijuana 22000, Mexico

[2] Univ Nacl Autonoma Mexico, Ctr Ciencias Mat Condensada, Ensenada 22800, Baja California, Mexico

来源：

SURFACE & COATINGS TECHNOLOGY | 2002年 / 154卷 / 2-3期

关键词：

corrosion; photoelectron spectroscopy; pulsed laser deposition; zinc alloy; yttrium oxide; tafel extrapolation;

D O I：

10.1016/S0257-8972(02)00030-0

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Samples of Zn-22Al-2Cu (zinalco) alloys with and without a thin film of Y2O3 were submitted to corrosion by potentiodynamic polarization and analyzed by means of X-ray photoelectron spectroscopy (XPS). In addition. corrosion current densities were measured by means of Tafel extrapolation of potentiodynamic polarization curves. After the corrosion process, all zinalco samples exhibit aluminum and zinc on the surface. Samples without the Y2O3 deposit show a depletion of aluminum on the surface, while samples with a 160-nm-thick Y2O3 film deposited by pulsed laser deposition (PLD) exhibit an aluminum-enriched surface and the formation of surface aluminum oxides. Samples with the Y2O3 deposited film and subjected to potentiodynamic polarization demonstrate an improvement in corrosion resistance up to 75% in pH=4.5 aerated water as compared with samples without the Y2O3 film. (C) 2002 Elsevier Science B.V All rights reserved.

引用

页码：218 / 222

页数：5

共 18 条

[11] The corrosion protection afforded by rare earth conversion coatings applied to magnesium [J].

Rudd, AL ;

Breslin, CB ;

Mansfeld, F .

CORROSION SCIENCE, 2000, 42 (02) :275-288

[12] Superplastic extrusion of microgear shaft of 10 μm in module [J].

Saotome, Y ;

Iwazaki, H .

MICROSYSTEM TECHNOLOGIES, 2000, 6 (04) :126-129

[13] HARTREE-SLATER SUBSHELL PHOTOIONIZATION CROSS-SECTIONS AT 1254 AND 1487EV [J].

SCOFIELD, JH .

JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1976, 8 (02) :129-137

[14] Effect of short glass fibers on the mechanical properties of cast ZA-27 alloy composites [J].

Sharma, SC ;

Seah, KHW ;

Satish, BM ;

Girish, BM .

MATERIALS & DESIGN, 1996, 17 (5-6) :245-250

[15] CALCULATIONS OF ELECTRON INELASTIC MEAN FREE PATHS .2. DATA FOR 27 ELEMENTS OVER THE 50-2000-EV RANGE [J].

TANUMA, S ;

POWELL, CJ ;

PENN, DR .

SURFACE AND INTERFACE ANALYSIS, 1991, 17 (13) :911-926

[16] WATER-VAPOR CORROSION OF LAMELLAR, SUPERPLASTIC AND CAST DENDRITIC ZN-21AL ALLOY [J].

TORRESVILLASENOR, G ;

UGALDE, A ;

HERNANDEZ, L ;

SINGER, IL .

CORROSION SCIENCE, 1984, 24 (03) :159-&

[17]

Villasenor G. T., 1985, REV MEX FIS, P489

[18] Modification of corrosion resistance by single and multi-element implantation into 304 stainless steel [J].

Weng, DA ;

Wang, M .

MATERIALS CHEMISTRY AND PHYSICS, 1998, 54 (1-3) :338-341

← 1 2 →