The effect of manganese and silicon additions on the corrosion resistance of a polycrystalline nickel-based superalloy

被引：29

作者：

Anzini, E. ^{[1
]}

Glaenzer, N. ^{[2
]}

Mignanelli, P. M. ^{[3
]}

Hardy, M. C. ^{[3
]}

Stone, H. J. ^{[2
]}

Pedrazzini, S. ^{[1
]}

机构：

[1] Imperial Coll London, Dept Mat, Exhibit Rd, London SW7 2AZ, England

[2] Univ Cambridge, Dept Mat Sci & Met, 27 Charles Babbage Rd, Cambridge CB3 0FS, England

[3] Rolls Royce Plc, POB 31, Derby DE24 8BJ, England

来源：

CORROSION SCIENCE | 2020年 / 176卷

基金：

英国工程与自然科学研究理事会;

关键词：

Nickel superalloy; Manganese; Silicon; Oxidation; Sulfur; Salt; Corrosion; HIGH-TEMPERATURE SULFIDATION; MORPHOLOGICAL DEVELOPMENT; HOT CORROSION; OXIDATION; MN; CHROMIUM; BEHAVIOR; SYSTEM; SO2; ATMOSPHERES;

D O I：

10.1016/j.corsci.2020.109042

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The service lives of nickel superalloys are often limited by environmental degradation. The present study compares oxidation, sulfidation and hot corrosion at 750 degrees C of three variants of a polycrystalline superalloy: a baseline alloy, a variant containing 1 wt% Mn and one containing 0.5 wt% Si. Mn reduced the oxidation rate without changing the scale morphology. The MnCr2O4 scale formed proved more protective against sulfidation and hot corrosion, but internal sulfides extended the damage depth. Si modified the oxide morphology to a continuous Cr2O3-Al2O3 dual layer. This provided improved protection, reducing the sulfidation depth by 2/3 and the hot corrosion depth by 1/2.

引用

页数：11

共 50 条

[41] Temperature-dependent deformation mechanisms and microstructural degradation of a polycrystalline nickel-based superalloy
Liu, Yahui
Wu, Yun
Yu, Junwei
Ju, Jiang
Zhang, Zhen
Kang, Maodong
Wang, Jun
Sun, Baode
Ning, Ying
JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 775 : 181 - 192
[42] Abnormal feather-like grains induced by the thin-wall effect in a polycrystalline nickel-based superalloy
Sun, Shijie
Sheng, Naicheng
Fan, Shigang
Ma, Yuejiao
Cao, Xi
Sang, Zhiru
Hou, Guichen
Li, Jinguo
Zhou, Yizhou
Sun, Xiaofeng
JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 901
[43] Development of strong, oxidation and corrosion resistant nickel-based superalloys: critical review of challenges, progress and prospects
Darolia, R.
INTERNATIONAL MATERIALS REVIEWS, 2019, 64 (06) : 355 - 380
[44] Cyclic Oxidation and Hot Corrosion Behavior of Nickel-Iron-Based Superalloy
Chellaganesh, D.
Khan, M. Adam
Jappes, J. T. Winowlin
Sathiyanarayanan, S.
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (02) : 173 - 180
[45] Effect of lanthanum on microstructure of a nickel-based single crystal superalloy
Gao, Hong
Guan, Kai
Cui, Ren-jie
Qin, Jian-chao
Zhao, Zi-han
Huang, Zhao-hui
CHINA FOUNDRY, 2025, 22 (01) : 55 - 64
[46] Investigation on the grain boundary strengthening effect of a nickel-based superalloy
Shi, Dongfang
Zhang, Zhenjun
Hu, Jinhai
Zhang, Zhefeng
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2021, 44 (03) : 822 - 831
[47] Influence of environmental factors on the corrosion-fatigue response of a nickel-based superalloy
Cockings, Hollie L.
Perkins, Karen M.
Dowd, Michael
MATERIALS SCIENCE AND TECHNOLOGY, 2017, 33 (09) : 1048 - 1055
[48] Effect of alloying elements on aqueous corrosion of nickel-based alloys at high temperatures: A review
Karimihaghighi, Razieh
Naghizadeh, Masoumeh
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2023, 74 (08): : 1246 - 1255
[49] The effect of porosity size and oxidation on the HCF property of nickel-based single crystal superalloy at 980 °C
Jiang, Wen
Li, Piao
Yao, Wei-Xing
Rui, Shao-Shi
Shi, Hui-Ji
Huang, Jie
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2022, 120
[50] The effect of salt composition on the stress-free and corrosion-fatigue performance of a fine-grained nickel-based superalloy
Hendery, M. L.
Whittaker, M. T.
Cockings, B. J.
Mignanelli, P. M.
CORROSION SCIENCE, 2022, 198

← 1 2 3 4 5 →